This paper presents a research dealing with the dependence of the fatigue strength of maraging steel parts, manufactured by direct selective laser sintering, on the production build orientation. Three sets of specimens have been manufactured according to the ISO 1143 Standard (2010) by EOSINT M280 additive manufacturing machine, with the following heat and mechanical treatments, in agreement with the recommendations by the material manufacturer and current literature. The expected outcomes are the Fatigue Limit values of the material and the maximum number of cycles observed at different stress levels for three different build orientations (three different angles, 0°, 45° and 90°, between the build direction and the longitudinal axis of the samples). The results have been processed and compared by statistical methods in order to determine the fatigue curves in the finite life domain and the fatigue limits, along with their confidence bands and intervals, and to investigate the significance of the build orientation factor.
The present study is focused on the fatigue strength of 15–5 PH stainless steel, built by Direct Metal Laser Sintering. Six‐specimen sets were manufactured, mechanically and thermally treated and tested under rotating bending fatigue. The study investigates the effects of the build orientation (parallel, perpendicular, or 45° inclined with respect to the vertical stacking direction) and of allowance for machining (1 mm or 3 mm at gage). The results, processed by an ANOVA methodology, indicate that allowance for machining has a beneficial effect on the fatigue response. Removing the surface irregularities, averagely leads to a 19% enhancement of the fatigue limit. The build orientation also becomes beneficial, when the slanted samples are included in the experiment. In this case, a fatigue strength increase up to 20% can be achieved. Further developments will include the investigation of the effects of heat and surface treatments, involving also further materials in the study.
The main motivations for this study arise from the need for an assessment of the fatigue performance of DMLS-produced Maraging Steel MS1, when it is used in the "as fabricated" state. The literature indicates a lack of knowledge from this point of view; moreover, the great potentials of the additive process may be more and more incremented, if an easier and cheaper procedure could be used after the building stage. The topic has been tackled experimentally, investigating the impact of heat treatment, machining, and micro-shot-peening on the fatigue strength with respect to the "as built state". The results indicate that heat treatment may improve the fatigue response, as an effect of the relaxation of the process-induced tensile residual stresses. Machining can also be effective, but it must be followed (not preceded) by shot-peening, to benefit from the compressive residual stress state generated by the latter. Moreover, heat treatment and machining are related by a strong positive interaction, meaning their effects are synergistically magnified when they are applied together. The experimental study has been completed by fractographic as well as micrographic analyses, investigating the impact of the heat treatment on the actual microstructure induced by the stacking process.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.