The main objective of this work is to evaluate the properties of hot asphalt mixtures that have been manufactured with different recycled concrete aggregate (RCA) percentages (0%, 20%, 40%, 60% and 80% of the fraction 5–13 mm) and asphalt (4%, 4.5% and 5%). Dense asphalt mixtures were made; partially replacing the natural aggregate (NA) fraction between 5 and 13 mm. Marshall specimens were manufactured to determine the main properties of the asphalt concrete (AC) in terms of density, voids, stability and deformation. Additionally, the optimal asphalt content (OAC) was determined, and measured the water sensibility, the stiffness modulus and the permanent deformation. The results corroborate the potential for using these sources of construction and demolition waste (CDW) as a RCA in asphalt concrete and show that the hot asphalt mixtures with up to 40% substitution of natural aggregate by recycled aggregate in the fraction 5–13 mm present good behavior.

Recycled Aggregates (RA) from construction and demolition waste (CDW) are a technically viable alternative to manufacture of asphalt concrete (AC). The main objective of this work is to evaluate the properties of hot asphalt mixtures that have been manufactured with different sources of CDW (material from concrete test specimens, material from the demolition of sidewalks and waste from prefabrication plants) from Cuba. Dense asphalt mixtures were manufactured with a maximum aggregate size of 19 mm, partially replacing (40%) the natural aggregate fraction measured between 5 mm and 10 mm with three types of RA from Cuba. Marshall specimens were manufactured to determine the main properties of the AC in terms of density, voids, stability and deformation. Additionally, the stiffness modulus of the AC was evaluated at 7 °C, 25 °C and 50 °C. The results corroborate the potential for using these sources of CDW from Cuba as a RA in asphalt concrete, thereby contributing an important environmental and economic benefit.

In Cuba, tons of construction and demolition waste (CDW) are generated during urban construction and reconstruction activities every year. The use of CDW, such as recycled concrete aggregates (RCA) and reclaimed asphalt pavement (RAP), in pavement construction is a viable solution to preserve the consumption of natural aggregates (NA), and to minimize the impact of landfill. The main objective of this work is to obtain a 5–10 mm aggregate fraction of RCA and RAP, to obtain an appropriate recycled coarse aggregate for manufacturing hot mix asphalt (HMA). Each source of RCA, RAP and NA, and the combinations RCA/RAP (0/100, 25/75, 50/50, 75/25 and 100/0) were characterized (moisture, asphalt content of RAP, specific gravity, water absorption, and flakiness index) for determining a better combination. The results showed that the combination (RCA/RAP) that best meets the NA aggregates specifications used for hot mix asphalt were RCA/RAP: 25/75 and 50/50. The results show the possibility of combining both wastes to obtain a coarse aggregate fraction with a high environmental benefit, by reducing the use of natural resources.