New aromatic (co)polyesters containing pendant propargyloxy groups were synthesized by phase transfer‐catalyzed interfacial polycondensation of 5‐(propargyloxy)isophthaloyl chloride (P‐IPC) and various compositions of P‐IPC and isophthaloyl chloride with bisphenol A. FTIR and NMR spectroscopic data, respectively, revealed successful incorporation of pendant propargyloxy groups into (co)polyesters and formation of (co)polyesters with desired compositions. (Co)polyesters exhibited good solubility in common organic solvents such as chloroform, dichloromethane, and tetrahydrofuran and could be cast into transparent, flexible, and tough films from chloroform solution. Inherent viscosities and number average molecular weights of (co)polyesters were in the range 0.77–1.33 dL/g and 43,600–118,000 g/mol, respectively, indicating the achievement of reasonably high‐molecular weights. The 10% weight loss temperatures of (co)polyesters were in the range 390–420 °C, demonstrating their good thermal stability. (Co)polyesters exhibited Tg in the range 146–170 °C and Tg values decreased with increase in mol % incorporation of P‐IPC. The study of non‐isothermal curing by DSC indicated thermal crosslinking of (co)polyesters via propargyloxy groups. The utility of pendant propargyloxy group was demonstrated by post‐modification of the selected copolyester with 1‐(4‐azidobutyl)pyrene, 9‐(azidomethyl)anthracene, and azido‐terminated poly(ethyleneglycol) monomethyl ether via copper(I)‐catalyzed Huisgen 1,3‐dipolar cycloaddition reaction. FTIR and 1H NMR spectra confirmed that click reaction was quantitative. © 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019, 57, 588–597

Expanding on our strategy to synthesize aromatic stepgrowth polymers containing pendant clickable azido groups via functional monomer approach, we have now designed and synthesized a new cardo bisphenol, viz., 2-(2-azidoethyl)-3, 3-bis(4-hydroxyphenyl) isoindolin-1-one (PPH-N 3 ). PPH-N 3 was conveniently synthesized starting from commercially available phenolphthalein by a three-step route in an overall yield of 65% using simple organic transformations. Aromatic (co)polyesters bearing pendant azido groups were synthesized by low-temperature solution polycondensation of PPH-N 3 or different molar ratios of PPH-N 3 and bisphenol-A (BPA) with aromatic diacid chlorides in dry dichloromethane in the presence of triethylamine (TEA) as a base. The formation of medium to reasonably high-molecular-weight (co)polyesters was evidenced from intrinsic viscosity and number-average molecular-weight measurements that were in the range 0.52-0.85 dL/g and 16,700-28,200, respectively. Tough, transparent, and flexible films could be cast from chloroform solutions of these (co)polyesters. (Co)polyesters were characterized using FTIR, 1 H NMR, 13 C NMR spectroscopy, XRD, and TGA. The thermal curing reaction of (co)polyesters involving decomposition of azido groups was studied by DSC analysis. The chemical modification of a representative copolyester containing pendant azido groups was carried out quantitatively using catalyst-free azide-maleimide cycloaddition reaction with two maleimides, namely, Nmethylmaleimide and N-hexylmaleimide.Additional supporting information may be found in the online version of this article.

No abstract