Alkali-activated binders (AABs) are developed through the activation of aluminosilicate-rich materials using alkaline reagents. The characteristics of AABs developed using a novel dry-mixing technique incorporating powder-based reagents/activators are extensively explored. A total of forty-four binder mixes are assessed in terms of their fresh and hardened state properties. The influence of mono/binary/ternary combinations of supplementary cementitious materials (SCMs)/precursors and different types/combinations/dosages of powder-based reagents on the strength and workability properties of different binder mixes are assessed to determine the optimum composition of precursors and the reagents. The binary (55% fly ash class C and 45% ground granulated blast furnace slag) and ternary (25% fly ash class C, 35% fly ash class F and 40% ground granulated blast furnace slag) binders with reagent-2 (calcium hydroxide and sodium sulfate = 2.5:1) exhibited desired workability and 28-day compressive strengths of 56 and 52 MPa, respectively. Microstructural analyses (in terms of SEM/EDS and XRD) revealed the formation of additional calcium aluminosilicate hydrate with sodium or mixed Ca/Na compounds in binary and ternary binders incorporating reagent-2, resulting in higher compressive strength. This research confirms the potential of producing powder-based cement-free green AABs incorporating binary/ternary combinations of SCMs having the desired fresh and hardened state properties under ambient curing conditions.

Alkali-activated mortars (AAMs) are developed incorporating binary/ternary combinations of industrial wastes comprising of fly ash class C (FA-C), fly ash class F (FA-F) and ground granulated blast furnace slag (GGBFS) with alkaline reagents and silica sand. The use of high calcium precursors, calcium-based powder form reagents, dry mixing method, and ambient curing with performance characterization based on chemical ratios and fracture properties are some novel aspects of the study. The mechanical (dry density, compressive strength, ultrasonic pulse velocity, elastic modulus, fracture/crack tip toughness and fracture energy), durability (shrinkage/expansion and mass change in water and ambient curing conditions, water absorption and freeze-thaw resistance) and microstructural (SEM/EDS and XRD analyses) characteristics of eight AAMs are investigated. The binary (FA-C + GGBFS) mortars obtained higher compressive strengths (between 35 MPa and 42.6 MPa), dry densities (between 2032 kg/m3 and 2088 kg/m3) and ultrasonic pulse velocities (between 3240 m/s and 4049 m/s) than their ternary (FA-C + FA-F + GGBFS) counterparts. The elastic modulus and fracture toughness for mortars incorporating reagent 2 (calcium hydroxide: sodium sulphate = 2.5:1) were up to 1.7 and five times higher than those with reagent 1 (calcium hydroxide: sodium metasilicate = 1:2.5). This can be attributed to the additional formation of C-S-H with C-A-S-H/N-C-A-S-H binding phases in mortars with reagent 2. Ternary mortars exhibited comparatively lower shrinkage/expansion and initial sorptivity indices than their binary counterparts due to the lower geopolymerisation potential of fly ash class F that facilitated the reduction of matrix porosity. All mortar specimens demonstrated 100% or more relative dynamic modulus of elasticity after 60 freeze-thaw cycles, indicating the damage recovery and satisfactory durability due to probable micro-level re-arrangement of the binding phases. This study confirmed the viability of producing cement-free AAMs with satisfactory mechanical and durability characteristics.

Ambient cured alkali-activated mortars (AAMs) are developed through the activation of supplementary cementitious materials (SCMs) by powder form reagents with silica sand using a novel dry-mixing method. The fresh state, rheological, compressive strength and microstructural characteristics of eight AAM mixes are comprehensively investigated. The effects of binary/ternary combinations/proportions of SCMs, different combinations/dosages of powder form reagents and the fundamental chemical ratios (SiO2/Al2O3, Na2O/SiO2, CaO/SiO2 and Na2O/Al2O3) present in the precursors and the reagents are investigated. The AAM mixes obtained compressive strengths ranging from 34 to 42.6 MPa with initial and final setting times between 122 and 458 min and 215 and 483 min, respectively. The yield stress and viscosity of the mixes decreased with the increase in the slump flow spread. All the mixes demonstrated pseudoplastic behavior. The microstructural analysis revealed the formation of more longer polymeric chains comprising Si-Al linkages in N-C-A-S-H/N-A-S-H gels for reagent one (calcium hydroxide:sodium metasilicate = 1:2.5) mixes, which resulted in a lower slump flow, higher yield stress, higher plastic viscosity and quicker setting times compared to their reagent two (calcium hydroxide:sodium sulfate = 2.5:1) counterparts.

Alkali-activated binders (AABs) are developed using a dry mixing method under ambient curing incorporating powder-form reagents/activators and industrial waste-based supplementary cementitious materials (SCMs) as precursors. The effects of binary and ternary combinations/proportions of SCMs, two types of powder-form reagents, fundamental chemical ratios (SiO2/Al2O3, Na2O/SiO2, CaO/SiO2, and Na2O/Al2O3), and incorporation of polyvinyl alcohol (PVA) fibers on fresh state and hardened characteristics of 16 AABs were investigated to assess their performance for finding suitable mix compositions. The mix composed of ternary SCM combination (25% fly-ash class C, 35% fly-ash class F, and 40% ground granulated blast furnace slag) with multi-component reagent combination (calcium hydroxide and sodium metasilicate = 1:2.5) was found to be the most optimum binder considering all properties with a 56 day compressive strength of 54 MPa. The addition of 2% v/v PVA fibers to binder compositions did not significantly impact the compressive strengths. However, it facilitated mitigating shrinkage/expansion strains through micro-confinement in both binary and ternary binders. This research bolsters the feasibility of producing ambient cured powder-based cement-free binders and fiber-reinforced, strain-hardening composites incorporating binary/ternary combinations of SCMs with desired fresh and hardened properties.

Differential privacy is one of the most popular technologies in the growing area of privacy-conscious data analytics. But differential privacy, along with other privacy-enhancing technologies, may enable privacy theater. In implementations of differential privacy, certain algorithm parameters control the tradeoff between privacy protection for individuals and utility for the data collector; thus, data collectors who do not provide transparency into these parameters may obscure the limited protection offered by their implementation. Through large-scale online surveys, we investigate whether explanations of differential privacy that hide important information about algorithm parameters persuade users to share more browser history data. Surprisingly, we find that the explanations have little effect on individuals' willingness to share data. In fact, most people make up their minds about whether to share before they even learn about the privacy protection.