Developments in the field of materials science are contributing to providing solutions for the recycling of industrial residues to develop new materials. Such approaches generate new products and provide optimal alternatives to the final disposal of different types of industrial wastes. This research focused on identifying and characterizing slag, fly ash, and glass cullet from the Boyacá region in Colombia as raw materials for producing glass-ceramics, with the innovative aspect of the use of these three residues without the addition of nucleating agents to produce the glass-ceramics. To characterize the starting materials, X-ray diffraction (XRD), X-ray fluorescence (XRF), and Scanning Electron Microscopy (SEM) techniques were used. The results were used to evaluate the best conditions to produce mixtures of the three waste components and to determine the specific compositions of glass-ceramics to achieve products with attractive technical properties for potential industrial applications. The proposed mixtures were based on three compositions: Mixture 1, 2, and 3. The materials were obtained through thermal treatment at 1200 °C in a tubular furnace in accordance with the results of a comprehensive characterization using thermal analysis. The microstructure, thermal stability, and structural characteristics of the samples were examined through SEM, differential thermal analysis (DTA), and XRD analyses, which showed that the main crystalline phases were diopside and anorthite, with a small amount of enstatite and gehlenite. The obtained glass-ceramics showed properties of technical significance for structural applications.

No abstract

Glass-ceramics are advanced inorganic silicate materials that can be obtained by sintering glass powders using a careful temperature control to result in the densification, nucleation, and crystallization of the material. In the current work, three different samples were obtained starting from amorphous silicate materials derived from mixtures of metallurgical slag, coal fly ash, and glass cullet, mixed in different proportions. The as-received waste samples were heat-treated to high temperatures to achieve complete melting at 1200, 1300, and 1400 °C for two hours, performing a rapid cooling in order to yield an amorphous material (glass). The obtained frit was ball-milled to a powder, which was then cold pressed to obtain compact pellets. The thermal treatment of pellets was carried out at 800–1100 °C for 2 h followed by a cooling rate of 10 °C/min to obtain the final glass-ceramics. The microstructure of samples was evaluated with scanning electron microscopy (SEM), which showed heterogeneous conglomerates and clusters of ~20 microns. The formation of crystalline phases was corroborated by means of X-ray diffraction (XRD) analysis, showing the presence of anorthite in all samples. Depending on the sample composition, other crystalline phases such as augite, enstatite, and diopside were detected. Using the Debye–Scherrer equation, it was possible to find the average size of the nano-crystalline domains. The quantification of the non-crystalline or amorphous fraction was also performed. Additionally, the density and porosity of the materials were calculated using the procedures defined in the ASTM C373 and ASTM C20 standards, measuring density values in the range 2.2–3.1 g·cm−3. The apparent porosity was approx. 33% in the three materials. Raman spectroscopy analysis showed characteristic signals associated with crystalline phases containing alumina, silica, iron, and calcium. Overall, the study confirmed the possibility of obtaining glass-ceramics with fine (nanometric) crystal sizes from a combination of silicate waste and the capability of modifying the crystalline composition by changing the proportions of the different wastes in the initial formulations.

No abstract