Two oxide-dispersion-strengthened (ODS) steels with different compositions (14Cr-ODS and 14Cr-Zr-ODS) were investigated to reveal the influences of microalloying element addition on the microstructure and to clarify the refining mechanism of precipitated particles. TEM and HRTEM results indicated that precipitated particles in the Zr-containing ODS steel had finer sizes and dispersed more homogeneously within the grains. It was found that rhombohedral Y4Zr3O12 particles with complex lattice structures were formed and could pin the migration of the grain boundaries during heat treatment due to their high thermal stability. In addition, the Zr-containing ODS steel exhibited a finer and more uniform grain morphology. Tensile tests showed that microalloying element addition could significantly improve the comprehensive mechanical properties of 14Cr ODS steels at room temperature.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.