Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) with various 3-hydroxyvalerate (3HV) contents biosynthesized by mixed microbial consortia (MMC) fed fermented dairy manure at the large-scale level was assessed over a 3-month period. The thermal, mechanical, and rheological behavior and the chemical structure of the extracted PHBV biopolymers were studied. The recovery of crude PHBV extracted in a large Soxhlet extractor with CHCl3 for 24 h ranged between 20.6% to 31.8% and purified to yield between 8.9% to 26.9% all based on original biomass. 13C-NMR spectroscopy revealed that the extracted PHBVs have a random distribution of 3HV and 3-hydroxybutyrate (3HB) units and with 3HV content between 16% and 24%. The glass transition temperature (Tg) of the extracted PHBVs varied between −0.7 and −7.4 °C. Some of the extracted PHBVs showed two melting temperatures (Tm) which the lower Tm1 ranged between 126.1 °C and 159.7 °C and the higher Tm2 varied between 152.1 °C and 170.1 °C. The weight average molar mass of extracted PHBVs was wide ranging from 6.49 × 105 g·mol−1 to 28.0 × 105 g·mol−1. The flexural and tensile properties were also determined. The extracted polymers showed a reverse relationship between the 3HV content and Young’s modulus, tensile strength, flexural modulus, and flexural strength properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.