Abstract:We synthesized polyethylene (PE), poly(ethylene-co-1-decene), poly (ethyleneco-p-methylstyrene) and poly(ethylene-ter-1-decene-ter-p-methystyrene) using a rac-Et(Ind) 2 ZrCl 2 metallocene catalyst and a methylaluminoxane cocatalyst system. The materials were characterized using nuclear magnetic resonance spectroscopy and Fourier transform infrared spectroscopy. We compared and studied the kinetics, thermal properties and mechanical ones of these polymers. T g was related to the amorphous phase of the polymers, whereas the tensile strength and storage modulus (E') were related to the crystalline phase. We also found that PE has the highest crystallinity through differential scanning calorimetry and wide-angle X-ray scattering analysis. The polymerization rates of poly(ethylene-co-1-decene) and poly(ethylene-ter-1-decene-ter-p-methystyrene) were always higher than that of polyethylene.

ABSTRACT：We synthesized polyethylene, poly(ethylene-co-1-decene), poly(ethylene-co-p-methylstyrene), and poly(ethylene-ter-1-decene-ter-p-methystyrene) using a rac-Et(Ind) 2 ZrCl 2 metallocene catalyst and a methylaluminoxane cocatalyst system. The materials were characterized using nuclear magnetic spectroscopy and fourier transform infrared spectroscopy. To identify suitable reaction conditions for terpolymerization, we studied the effects of catalyst content, cocatalyst/catalyst molar ratio, polymerization time, and polymerization temperature. As the catalyst content increased, the catalytic activity and the molecular weight of the terpolymers increased. The catalytic activity sharply increased but little change was observed after a polymerization time of 30 min. The increase in the cocatalyst/catalyst molar ratio resulted in a decrease in the molecular weight of the terpolymers and an increase in the catalytic activity to some degree. The catalytic activity increased with increasing polymerization temperature, while the molecular weight of the terpolymers decreased. 요 약：rac-Et(Ind)2 ZrCl