The scalable preparation of two-dimensional hexagonal boron nitride (h-BN) is essential for practical applications. Despite intense research in this area, high-yield production of two-dimensional h-BN with large-size and high solubility remains a key challenge. In the present work, we propose a scalable exfoliation process for hydroxyl-functionalized BN nanoplatelets (OH-BNNPs) by a simple ball milling of BN powders in the presence of sodium hydroxide via the synergetic effect of chemical peeling and mechanical shear forces. The hydroxide-assisted ball milling process results in relatively large flakes with an average size of 1.5 μm with little damage to the in-plane structure of the OH-BNNP and high yields of 18%. The resultant OH-BNNP samples can be redispersed in various solvents and form stable dispersions that can be used for multiple purposes. The incorporation of the BNNPs into the polyethylene matrix effectively enhanced the barrier properties of the polyethylene due to increased tortuosity of the diffusion path of the gas molecules. Hydroxide-assisted ball milling process can thus provide simple and efficient approaches to scalable preparation of large-size and highly soluble BNNPs. Moreover, this exfoliation process is not only easily scalable but also applicable to other layered materials.

The influence of surface modifications on the mechanical properties of epoxy-hexagonal boron nitride nanoflake (BNNF) nanocomposites is investigated. Homogeneous distributions of boron nitride nanoflakes in a polymer matrix, preserving intrinsic material properties of boron nitride nanoflakes, is the key to successful composite applications. Here, a method is suggested to obtain noncovalently functionalized BNNFs with 1-pyrenebutyric acid (PBA) molecules and to synthesize epoxy-BNNF nanocomposites with enhanced mechanical properties. The incorporation of noncovalently functionalized BNNFs into epoxy resin yields an elastic modulus of 3.34 GPa, and 71.9 MPa ultimate tensile strength at 0.3 wt%. The toughening enhancement is as high as 107% compared to the value of neat epoxy. The creep strain and the creep compliance of the noncovalently functionalized BNNF nanocomposite is significantly less than the neat epoxy and the nonfunctionalized BNNF nanocomposite. Noncovalent functionalization of BNNFs is effective to increase mechanical properties by strong affinity between the fillers and the matrix.

We report boron nitride nanoflakes (BNNFs), for the first time, as a nanofiller for polymer electrolyte membranes in fuel cells. Utilizing the intrinsic mechanical strength of two-dimensional (2D) BN, addition of BNNFs even at a marginal content (0.3 wt %) significantly improves mechanical stability of the most representative hydrocarbon-type (HC-type) polymer electrolyte membrane, namely sulfonated poly(ether ether ketone) (sPEEK), during substantial water uptake through repeated wet/dry cycles. For facile processing with BNNFs that frequently suffer from poor dispersion in most organic solvents, we non-covalently functionalized BNNFs with 1-pyrenesulfonic acid (PSA). Besides good dispersion, PSA supports efficient proton transport through its sulfonic functional groups. Compared to bare sPEEK, the composite membrane containing BNNF nanofiller exhibited far improved long-term durability originating from enhanced dimensional stability and diminished chronic edge failure. This study suggests that introduction of properly functionalized 2D BNNFs is an effective strategy in making various HC-type membranes sustainable without sacrificing their original adventurous properties in polymer electrolyte membrane fuel cells.

No abstract