We have prepared and combined ZnO nanoparticles (ZnO-NPs) with different graphene oxide (GO) contents (10%, 20% and 30%) via microwave processing. The procedure provided well-dispersed ZnO-NPs between and onto the rGO layers (GZCs). The annealing temperature and graphene oxide contents affected the UV-Vis absorption, PL emission, defect-states of the ZnO, EPR signals, photo-electrochemical response and charge transfer properties. The HRTEM microscopy images of the GZCs showed interpenetrating structures and clearly visible vacancy defects. The results indicated that the defect sites (Zn interstitials, oxygen vacancy, ionized zinc vacancy and oxygen interstitials) significantly decreased after hybridization with GO. The photo-conversion efficiency of the GZC-10% (η = 13.1 x 10-3%), is 13 times higher than the ZnO-NPs (η = 1.02 x 10-3%) illustrating higher exciton production and separation efficiency of the GZCs under photo-excitation. The GZC-10% has lower (8-15 Ω) charge transfer resistance (Rct) compared to all the GZCs under same experimental conditions, therefore an important reason of better performance of the GZC 10%. The EPR spectra showed presence of radicals in all the samples with GZC 10% most intense signal among the different GZCs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.