The compatibilizing effect of poly(styrene-co-acrylonitrile) (SAN) whose acrylonitrile (AN) content is 25 wt % (SAN 25) in poly(acrylonitrile-co-butadiene-costyrene) (ABS)/poly(vinyl chloride) (PVC) blend was studied when the AN content of the matrix SAN in ABS was 35 wt % (SAN 35). When some amount of matrix SAN 35 was replaced by SAN 25 in a ABS/PVC (50/50 by weight) blend, the mixed phase of SAN and PVC at the interface was thickened, and about a twofold increase of impact strength was observed. The changes in morphology, dynamic mechanical properties, and rheological properties by the compatibilizing effect of SAN 25 were observed.

ABSTRACT:The effects of blend composition, melt viscosity of poly(acrylonitrile-butadiene-styrene) (ABS), and compatibilizing effect of poly(methyl methacrylate) (PMMA) on mechanical properties of ABS/polycarbonate (PC) blends at ABS-rich compositions were studied. As the content of PC was increased, impact strength and Vicat softening temperature (VST) were increased. As the melt viscosity of ABS was increased near to that of PC, finer distribution of dispersed PC phase and consequent enhanced impact strength and VST were observed. The compatibilizing effect of PMMA can be ascertained from the enhanced properties of 1 4 -inch notch impact strength, VST, tensile strength, and the morphology observed by a scanning electron microscope. The improved adhesion of the ABS/PC interface by PMMA changed the fracture mechanism and reduced the notch sensitivity of blends.

The compatibilizing effect of poly(styrene-co-acrylonitrile) (SAN) whose acrylonitrile (AN) content is 25 wt % (SAN 25) in poly(acrylonitrile-co-butadiene-costyrene) (ABS)/poly(vinyl chloride) (PVC) blend was studied when the AN content of the matrix SAN in ABS was 35 wt % (SAN 35). When some amount of matrix SAN 35 was replaced by SAN 25 in a ABS/PVC (50/50 by weight) blend, the mixed phase of SAN and PVC at the interface was thickened, and about a twofold increase of impact strength was observed. The changes in morphology, dynamic mechanical properties, and rheological properties by the compatibilizing effect of SAN 25 were observed.