An investigation on the structure of poly(o-phenylenediamine) (PPD) films, obtained by electropolymerization of oPD (1,2-diaminobenzene) on platinum at different pH values, was performed by X-ray Photoelectron Spectroscopy (XPS).XPS could be used as a ''bulk'' technique for PPD films analysis, due to their extremely low thickness. The presence of different functionalities, like primary/secondary aminic, iminic and, as minor species, oxygenated groups (carbonyl, oximes) was suggested by curve fitting of carbon (C1s) and nitrogen (N1s) XP spectra. The use of chemical derivatization reactions (CD-XPS) confirmed the presence of primary aminic and hydroxy groups, showing that NH 2 groups are present in the PPD structure even at low pH values, though their amount increases on increasing the pH of polymerization.Optical spectroscopy in the visible region was also performed on the electrolytic solutions at the end of polymerization, suggesting a higher conjugation of the oPD oligomers at low pH, which indirectly confirms XPS findings on the presence of NH 2 groups in the polymer.

No abstract

No abstract

The electrosynthesis of copper and silver core-shell nanoparticles (NPs) by the sacrificial anode technique, employing tetraoctylammonium (TOA) salts as base electrolyte for the first time, is described. These surfactants were selected because they combine high NP stabilizing power with useful disinfecting properties. The resulting colloids were mixed with a solution of an inert dispersing polymer and used to prepare nanostructured composite thin films. The morphologies and chemical compositions of the nanomaterials were characterized by Transmission Electron Microscopy (TEM) and X-ray Photoelectron Spectroscopy (XPS). The TEM reveals that the average core diameter of the metal NPs ranges between 1.7 and 6.3 nm, as a function of the nature of the metal and of the electrosynthesis conditions, and does not change significantly upon inclusion in the polymer matrix. An appreciable concentration of the metal is detected on the nanoparticle surface by XPS. High-resolution XP spectra indicate that both copper and silver are present at zero oxidation state in all of the materials (colloids and composite films). This demonstrates the high efficiency of the surfactant at controlling the morphology and the chemical composition of the nanodispersed metal in both the as-synthesized colloid and in the polymeric dispersion. The nanocoatings are shown to exert a marked inhibitory effect on the growth of eukaryote and prokaryote target microrganisms, and experimental evidence of a synergic disinfecting effect due to the surfactant and the nanodispersed metal is provided. On the basis of these stability and bioactivity results, it is clear that Cu-NPs and Ag-NPs are suitable for application in disinfecting or antifouling paint and coating formulations.

The covalent attachment of an Arg-Gly-Asp (RGD) containing peptide to polypyrrole(PPy)-coated titanium substrates has been investigated in order to develop a bioactive material of potential use in orthopedic fields. Polypyrrole has been employed as the coating polymer because of its suitability to be electrochemically grown directly onto metallic substrates of different shapes, leading to remarkably adherent films. The synthetic peptide Cys-Gly-(Arg-Gly-Asp)-Ser-Pro-Lys, containing the cell-adhesive region of fibronectin (RGD), has been grafted to the polymer substrate via the cysteine residue using a procedure recently developed in the authors laboratory. The effectiveness of grafting was monitored by X-ray photoelectron spectroscopy (XPS), which assessed the presence of the peptide grafted onto the polymer surface exploiting the cysteine sulfur as target element. Neonatal rat calvarial osteoblasts were attached to RGD-modified PPy-coated Ti substrates at levels significantly greater than on unmodified PPy-coated Ti and glass coverslip substrates.