Background A novel injectable mixture termed treated dentin matrix hydrogel (TDMH) has been introduced for restoring dentin defect in DPC. However, no study evaluated its physiological biodegradation. Therefore, the present study aimed to assess scaffold homogeneity, mechanical properties and biodegradability in vitro and in vivo and the regenerated dentin induced by TDMH as a novel pulp capping agent in human permanent teeth. Methods Three TDMH discs were weighted, and dry/wet ratios were calculated in four slices from each disc to evaluate homogeneity. Hydrogel discs were also analyzed in triplicate to measure the compressive strength using a universal testing machine. The in vitro degradation behavior of hydrogel in PBS at 37 °C for 2 months was also investigated by monitoring the percent weight change. Moreover, 20 intact fully erupted premolars were included for assessment of TDMH in vivo biodegradation when used as a novel injectable pulp capping agent. The capped teeth were divided into four equal groups according to extraction interval after 2-, 8-, 12- and 16-weeks, stained with hematoxylin–eosin for histological and histomorphometric evaluation. Statistical analysis was performed using F test (ANOVA) and post hoc test (p = 0.05). Results No statistical differences among hydrogel slices were detected with (p = 0.192) according to homogeneity. TDMH compression modulus was (30.45 ± 1.11 kPa). Hydrogel retained its shape well up to 4 weeks and after 8 weeks completely degraded. Histological analysis after 16 weeks showed a significant reduction in TDMH area and a simultaneous significant increase in the new dentin area. The mean values of TDMH were 58.8% ± 5.9 and 9.8% ± 3.3 at 2 and 16 weeks, while the new dentin occupied 9.5% ± 2.8 at 2 weeks and 82.9% ± 3.8 at 16 weeks. Conclusions TDMH was homogenous and exhibited significant stability and almost completely recovered after excessive compression. TDMH generally maintained their bulk geometry throughout 7 weeks. The in vivo response to TDMH was characterized by extensive degradation of the hydrogel and dentin matrix particles and abundant formation of new dentin. The degradation rate of TDMH matched the rate of new dentin formation. Trial registration: PACTR201901866476410: 30/1/2019.

Background In recent years, treated dentin matrix (TDM) has been introduced as a bioactive hydrogel for dentin regeneration in DPC. However, no study has introduced TDM as a photocrosslinkable hydrogel with a natural photoinitiating system. Therefore, the present study aimed to explore the synthesis, characterizations and grafting optimization of injectable gelatin- glycidyl methacrylate (GMA)/TDM hydrogels as a novel photocrosslinkable pulp capping agent for dentin regeneration. Methods G-GMA/TDM hydrogel was photocrosslinked using a new two-component photoinitiating system composed of riboflavin as a photoinitiator under visible light and glycine as a first time coinitiator with riboflavin. The grafting reaction conditions of G-GMA/TDM e.g. GMA concentration and reaction time were optimized. The kinetic parameters e.g. grafting efficiency (GE) and grafting percentage (GP%) were calculated to optimize the grafting reaction, while yield (%) was determined to monitor the formation of the hydrogel. Moreover, G-GMA/TDM hydrogels were characterized by swelling ratio, degradation degree, and cytotoxicity. The instrumental characterizations e.g. FTIR, 1H-NMR, SEM and TGA, were investigated for verifying the grafting reaction. Statistical analysis was performed using F test (ANOVA) and Post Hoc Test (P = 0.05). Results The grafting reaction dramatically increased with an increase of both GMA concentration and reaction time. It was realized that the swelling degree and degradation rate of G-GMA/TDM hydrogels were significantly reduced by increasing the GMA concentration and prolonging the reaction time. When compared to the safe low and moderate GMA content hydrogels (0.048, 0.097 M) and shorter reaction times (6, 12, 24 h), G-GMA/TDM with high GMA contents (0.195, 0.391 M) and a prolonged reaction time (48 h) demonstrated cytotoxic effects against cells using the MTT assay. Also, the morphological surface of G-GMA/TDM freeze-dried gels was found more compacted, smooth and uniform due to the grafting process. Significant thermal stability was noticed due to the grafting reaction of G-GMA/TDM throughout the TGA results. Conclusions G-GMA/TDM composite hydrogel formed by the riboflavin/glycine photoinitiating system is a potential bioactive and biocompatible system for in-situ crosslinking the activated-light pulp capping agent for dentin regeneration.