Abstract:In this study, four samples of recycled aggregates from the construction and demolition waste of Mexico City were characterized in order to find innovative uses for these types of materials. Gravel and sand from a recycling plant were analyzed, as well as aggregates produced in the laboratory from demolished concrete collected from landfills. The characterization was carried out by means of XRD (X-ray Diffraction), chemical microanalysis (EDS), X-ray fluorescence (XRF), pH measurement, and sieve analysis. The minerals present in the analyzed materials were feldspars, cristobalite and pyroxene, which corresponded to the natural aggregates, as well as variable amounts of calcite, a product of the carbonation of the cement paste adhered to these aggregates, and in a smaller proportion, calcium hemicarboaluminate, rosenhanite, and tobermorite. The quality (amount of cement) of the original concrete has a great influence on the granulometry and the chemical-mineralogical composition of the aggregates, since there will be different quantities and qualities of the cement paste adhered to the aggregates depending on their size. Finally, the pH values measured in all samples fluctuated between 10.15 and 12.08, suggesting that these materials can be used in soil stabilization or in agricultural applications.
En este trabajo se estudió el impacto térmico y estructural que genera la presencia del aserrín al ser utilizado como sustituto de una parte del volumen del agregado fino de la mezcla de los morteros para definir la cantidad máxima de esta fibra orgánica que se puede integrar a la mezcla del material antes de que el producto final deje de presentar una resistencia estructural aceptable. Para lograrlo, se determinó y comparó la resistencia a la compresión y el coeficiente de conducción térmica de tres morteros experimentales elaborados con agregado de aserrín, con respecto a los datos de una mezcla control sin presencia de aserrín. De este modo, se concluyó que la máxima cantidad de aserrín que debe integrarse a un mortero es del 25%, ya que este material presento una reducción del 26% de su coeficiente de conductividad térmica y una resistencia aceptable en comparación con la de otros concretos ligeros que se utilizan actualmente como acabados arquitectónicos.
In this study, four samples of recycled aggregates from construction and demolition waste of Mexico City were characterized, in order to find innovative uses for this type of materials. Gravel and sand from a recycling plant were analyzed, as well as recycled aggregates in the laboratory from demolished concrete collected in landfills. The characterization was carried out by means of XRD, chemical microanalysis (EDS), pH measurement and sieve analysis. The results reveal that the minerals present in the analyzed materials are triclinic feldspars, cristobalite and pyroxene which correspond to the natural aggregates, as well as variable amounts of calcite, product of the carbonation of the cement paste adhered to these aggregates and in a smaller proportion calcium hemicarboaluminate, rosenhanite and tobermorite. It was determined that the quality (amount of cement) of the original concrete that was recycled, has great influence on the granulometry and the chemical-mineralogical composition of the aggregates, since there will be different quantities and qualities of cement paste adhered to the aggregates of according to size. Finally the pH values measured in all samples fluctuate between 10.15 and 12.08, therefore it is suggested that these materials can be used in soil stabilization.
En este artículo se estudiaron las características de un mortero puzolánico, el cual se generó sustituyendo dentro de la mezcla un porcentaje del volumen de la arena por uno similar de diatomita, perlita o zeolita. Esto se realizó con el objetivo de definir a través de pruebas de laboratorio, los cambios generados por dicha modificación en el coeficiente de conducción térmica del material, así como su resistencia a la compresión. Todo esto se realizó porque si bien, las puzolanas naturales se han estudiado previamente como una opción para crear concretos ecológicos o elementos arquitectónicos aligerados, no se ha establecido claramente cuál es el aporte que estas pueden generar en la parte térmica hacia las pastas cementantes. Por último, la validación experimental demostró que la zeolita fue el mineral con el que se generaron las muestras de mortero con mejor relación entre la mejora del coeficiente de conducción térmica del material con respecto a una mínima reducción de su resistencia mecánica.
El presente trabajo tiene como objetivo caracterizar de forma preliminar por medio de difracción de rayos X, y MEB-EDS un suelo (feozem háplico) de la cuenca del Rio de la Avenidas al sur de la ciudad de Pachuca. El sitio de muestreo se eligió mediante el análisis de ortofotos, y apoyándose con diversos recorridos por el área, se obtuvo una muestra representativa de una pared de corte en una obra de infraestructura de acuerdo a la normatividad de la SCT. La muestra previo cuarteo y preparación se analizó por medio de DRX, determinándose que la mineralogía de este suelo está dominada por cuarzo (01-082-0511), y en mediana y menor proporción cuarzo α de alta presión (01- 079-1914) y caolinita (00-003-0059), así como una pequeña proporción de albita (99-100-0713), es importante señalar que el cuarzo α posee una alta densidad con respecto al cuarzo dominante. En tanto, por medio de MEB se observó la típica macla de albita en algunas muestras, así mismo, los análisis por medio de EDS mostraron la afinidad félsica de la muestra. De acuerdo a lo anterior y considerando la importancia del clima y del material parental como factores en la formación del suelo, se tiene que para la precipitación pluvial anual de la ciudad de Pachuca y con la herencia de la formaciones geológicas que suministraron el material (rocas félsicas predominantemente), lacaolinita es el mineral de arcilla presente en este suelo.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.