Effective skeletal muscle tissue engineering relies on control over the scaffold architecture for providing muscle cells with the required directionality, together with a mechanical property match with the surrounding tissue. Although recent advances in 3D printing fulfill the first requirement, the available synthetic polymers either are too rigid or show unfavorable surface and degradation profiles for the latter. In addition, natural polymers that are generally used as hydrogels lack the required mechanical stability to withstand the forces exerted during muscle contraction. Therefore, one of the most important challenges in the 3D printing of soft and elastic tissues such as skeletal muscle is the limitation of the availability of elastic, durable, and biodegradable biomaterials. Herein, we have synthesized novel, biocompatible and biodegradable, elastomeric, segmented polyurethane and polyurethaneurea (TPU) copolymers which are amenable for 3D printing and show high elasticity, low modulus, controlled biodegradability, and improved wettability, compared to conventional polycaprolactone (PCL) and PCL-based TPUs. The degradation profile of the 3D printed TPU scaffold was in line with the potential tissue integration and scaffold replacement process. Even though TPU attracts macrophages in 2D configuration, its 3D printed form showed limited activated macrophage adhesion and induced muscle-like structure formation by C2C12 mouse myoblasts in vitro, while resulting in a significant increase in muscle regeneration in vivo in a tibialis anterior defect in a rat model. Effective muscle regeneration was confirmed with immunohistochemical assessment as well as evaluation of electrical activity produced by regenerated muscle by EMG analysis and its force generation via a custom-made force transducer. Micro-CT evaluation also revealed production of more muscle-like structures in the case of implantation of cell-laden 3D printed scaffolds. These results demonstrate that matching the tissue properties for a given application via use of tailor-made polymers can substantially contribute to the regenerative outcomes of 3D printed tissue engineering scaffolds.

Since the dissolution of polyolefins is a chronic problem, melt processing has been tacitly accepted as an obligation. In this work, polypropylene (PP) was modified on molecular level incorporating poly(ethylene glycol) (PEG) as graft segment (PP-g-PEG) in a range of 6 to 9 mol%. Gold nanoparticles were nucleated in the presence of the copolymer chains via redox reaction. The dissolution of the amphiphilic comb-type graft copolymers containing gold nanoparticles (80 nm in diameter) was achieved in toluene and successfully electrospun from its solution. The diameter of composite fibers was in the range from 0.3 to 2.5 µm. The design of the structurally organized copolymer fiber mats provided a support medium for the nanoparticles enhancing the active surface area for the catalytic applications. The resulting composite fibers exhibited rapid catalytic reduction of methylene blue (MB) dye in the presence of sodium borohydride (NaBH 4 ) compared to corresponding composite cast film.

Polydopamine (PDA) nanoparticles are versatile structures that can be stabilized with proteins. In this study, we have demonstrated the feasibility of developing PDA/polypeptides complexes in the shape of nanoparticles. The polypeptide can also render the nanoparticle functional. Herein, we have developed antimicrobial nanoparticles with a narrow size distribution by decorating the polydopamine particles with a chain-length controlled antimicrobial agent Polyarginine (PAR). The obtained particles were 3.9 ± 1.7 nm in diameter and were not cytotoxic at 1:20 dilution and above. PAR-decorated nanoparticles have exhibited a strong antimicrobial activity against S. aureus, one of the most common pathogen involved in implant infections. The minimum inhibitory concentration is 5 times less than the cytotoxicity levels. Then, PAR-decorated nanoparticles have been incorporated into gelatin hydrogels used as a model of tissue engineering scaffolds. These nanoparticles have given hydrogels strong antimicrobial properties without affecting their stability and biocompatibility while improving their mechanical properties (modulus of increased storage). Decorated polydopamine nanoparticles can be a versatile tool for the functionalization of hydrogels in regenerative medicine applications by providing bioactive properties.