The application of liquid‐exfoliated 2D transition metal disulfides (TMDs) as the hole transport layers (HTLs) in nonfullerene‐based organic solar cells is reported. It is shown that solution processing of few‐layer WS2 or MoS2 suspensions directly onto transparent indium tin oxide (ITO) electrodes changes their work function without the need for any further treatment. HTLs comprising WS2 are found to exhibit higher uniformity on ITO than those of MoS2 and consistently yield solar cells with superior power conversion efficiency (PCE), improved fill factor (FF), enhanced short‐circuit current (JSC), and lower series resistance than devices based on poly(3,4‐ethylenedioxythiophene):poly(styrenesulfonate) and MoS2. Cells based on the ternary bulk‐heterojunction PBDB‐T‐2F:Y6:PC71BM with WS2 as the HTL exhibit the highest PCE of 17%, with an FF of 78%, open‐circuit voltage of 0.84 V, and a JSC of 26 mA cm−2. Analysis of the cells' optical and carrier recombination characteristics indicates that the enhanced performance is most likely attributed to a combination of favorable photonic structure and reduced bimolecular recombination losses in WS2‐based cells. The achieved PCE is the highest reported to date for organic solar cells comprised of 2D charge transport interlayers and highlights the potential of TMDs as inexpensive HTLs for high‐efficiency organic photovoltaics.

We report on bulk-heterojunction (BHJ) organic photovoltaics (OPVs) based on the self-assembled monolayer (SAM) 2PACz as a hole-selective interlayer functionalized directly onto the indium tin oxide (ITO) anode. The 2PACz is found to change the work function of ITO while simultaneously affecting the morphology of the BHJ deposited atop. Cells with PM6:N3 BHJ and ITO-2PACz anode exhibit a power conversion efficiency (PCE) of 16.6%, which is greater than that measured for bare ITO (6.45%) and ITO/PEDOT:PSS (15.94%) based devices. The enhanced performance is attributed to lower contact-resistance, reduced bimolecular recombination losses, and improved charge transport within the BHJ. Importantly, the ITO-2PACz-based OPVs show dramatically improved operational stability when compared with PEDOT:PSS-based cells. When the ITO-2PACz anode is combined with the ternary PM6:BTP-eC9:PC 71 BM BHJ, the resulting cells exhibit a maximum PCE of 18.03%, highlighting the potential of engineered SAMs for use in hole-selective contacts in high-performance OPVs.

Perovskite nanocrystals (NCs) have become leading candidates for solution-processed optoelectronics applications. While substantial work has been published on 3-D perovskite phases, the NC form of the zero-dimensional (0-D) phase of this promising class of materials remains elusive. Here we report the synthesis of a new class of colloidal semiconductor NCs based on CsPbBr, the 0-D perovskite, enabled through the design of a novel low-temperature reverse microemulsion method with 85% reaction yield. These 0-D perovskite NCs exhibit high photoluminescence quantum yield (PLQY) in the colloidal form (PLQY: 65%), and, more importantly, in the form of thin film (PLQY: 54%). Notably, the latter is among the highest values reported so far for perovskite NCs in the solid form. Our work brings the 0-D phase of perovskite into the realm of colloidal NCs with appealingly high PLQY in the film form, which paves the way for their practical application in real devices.

Zero-dimensional perovskite-related structures (0D-PRS) are a new frontier of perovskite-based materials. 0D-PRS, commonly synthesized in powder form, manifest distinctive optical properties such as strong photoluminescence (PL), narrow emission linewidth, and high exciton binding energy. These properties make 0D-PRS compelling for several types of optoelectronic applications, including phosphor screens and electroluminescent devices. However, it would not be possible to rationally design the chemistry and structure of these materials, without revealing the origins of their optical behaviour, which is contradictory to the well-studied APbX3 perovskites. In this work, we synthesize single crystals of Cs4PbBr6 0D-PRS, and investigated the origins of their unique optical and electronic properties. The crystals exhibit a PL quantum yield higher than 40%, the highest reported for perovskite-based single crystals. Time-resolved and temperature dependent PL studies, supported by DFT calculations, and structural analysis, elucidate an emissive behaviour reminiscent of a quantum confined structure rather than a typical bulk perovskite material.

Molecular doping has recently been shown to improve the operating characteristics of organic photovoltaics (OPVs). Here, we prepare neutral Diquat (DQ) and use it as n-dopant to improve the performance of state-of-the-art OPVs. Adding DQ in ternary bulk-heterojunction (BHJ) cells based of PM6:Y6:PC 71 BM is found to consistently increase their power conversion efficiency (PCE) from 16.7 to 17.4%. Analyses of materials and devices reveal that DQ acts as n-type dopant and morphology modifier for the BHJ leading to observable changes in its surface topography. The resulting n-doped BHJs exhibit higher optical absorption coefficients, balanced ambipolar transport, longer carrier lifetimes and suppressed bimolecular recombination, which are ultimately responsible for the increased PCE. The use of DQ was successfully extended to OPVs based on PM6:BTP-eC9:PC 71 BM for which a maximum PCE of 18.3% (uncertified) was achieved. Our study highlights DQ as a promising dopant for application in next generation organic solar cells.