In this study, physical and mechanical properties of pumice aggregate substituted with brick flour as mineral additive and light mortars were investigated. At the preparation of mortars, pumice (0-4mm) as a fine aggregate and CEM I 42.5R Portland Cement were used. Standard mortar mixing ratios were taken as fine aggregate/Cement/Water=3/1/0.5 and pumice aggregate is used as a fine aggregate. Brick flour, which is used as mineral additive, is substituted with 0%, 10%, 20% and 30% by weight of cement. The flow values of produced mortars were determined while they were in fresh form. Mortar samples were cured in standard cure pool for 28 days. Flexural and compressive strengths of the mortar samples which were cured for 7 days, were measured. Physical properties such as water absorption, porosity and unit volume weight of 28 days cured mortars were determined and flexural and compressive strengths were calculated. At the end of 28th day samples which were reached its final strength, were exposed to 200 ⁰C, 400 ⁰C, 600 ⁰C and 800 ⁰C heats in High Temperature Oven. With determining of flexural and compressive strengths after heating, strength loss between before and after heating was designated. It is observed that the flexural and compressive strengths were decreased with increasing the ratio of Brick Flour. At all temperatures, it is occurred that the ultrasound speed was decreased. With increasing of temperatures, ultrasound speed values were reduced.

İnşaat sektörünün önemli malzemelerinden biri olan çimento üretimi için yüksek miktarlarda enerji harcanmaktadır. İnşaat sektöründe çok fazla kullanım alanı olan çimentolu kompozitler için alternatif olabilecek çevreci çözümler tercih edilebilir. Çimento kullanılmadan üretilecek yapı malzemeleri çimento üretim miktarını azaltarak küresel ısınmanın zararlı etkilerini azaltacaktır. Üretilecek çevreci ürünlerin dayanım ve durabilite özellikleri açısından hâlihazırda kullanılan yapı malzemelerinin yerine geçebilecek nitelikte olması beklenmektedir. Bu çalışmada demir çelik fabrikalarının bir atığı olan Öğütülmüş Yüksek Fırın Cürufu (ÖYFC), Sodyum Hidroksit (NaOH), Sodyum Silikat (Na 2 SiO 3), agrega, hiperakışkanlaştırıcı ve su kullanılarak yüksek dayanımlı (65-85 MPa) jeopolimer betonlar üretilmiştir. Sertleşmiş jeopolimer numuneler, asit saldırılarına karşı dayanıklılık özelliklerini belirlemek amacıyla 0,5M, 1M ve 1,5 M'lik Sülfürik Asit (SA) çözeltisi içerisinde 1, 7, 14, 21 ve 28 gün süresince asit etkisine maruz bırakılmıştır. Jeopolimer numunelerin ağırlık kayıpları, su emme ve porozite değerleri belirlenmiştir. Sonuç olarak numunelerin asitte kalma süreleri arttıkça su emme, porozite ve ağırlık kayıp oranlarında artış gözlemlenmiştir. Su emme-ağırlık kaybı arasındaki ilişkiye benzer şekilde su emme ve porozite arasında da istatiksel olarak doğrusal bir ilişki olduğu görülmüştür.

This paper focuses on the electrical, physical and mechanical characterization of the ancient mortar (khorasan mortar) materials of precious structures, the Ali Paşa bathhouse, Çandarlı İbrahim Paşa bathhouse, Hasan Paşa bathhouse, Iznik Castle and Tophane rampart historical constructions located in the West of Turkey, in Bursa. An exhaustive description of the materials has been obtained to enriching the knowledge on historical construction materials. The definition of the physical and mechanical properties of the materials, sophisticated laboratory tests were performed such as compressive strength, point loading, weight loss in acid, specific porosity, density and water absorption tests. Microstructure investigations and electrical resistivity measurements were also performed on the ancient mortars. The good correlations were obtained between electrical resistivity and mechanical properties of historical mortars as result of relations between them. The experimental investigation has allowed a better understanding of the remote origin of these structures.

No abstract

Özet: Elektriksel özdirenç ölçümleri farklı mühendislik dallarında ihtiyaç duyulan bilgilerin bir kısmının sağlanması için oldukça fayda sağlamaktadır. Bu çalışmada kendiliğinden yerleşen harçlarda kullanılan yüksek fırın cürufu, uçucu kül, silis dumanı, tuğla tozu ve kırmataş tozu gibi mineral katkıların elektriksel özdirenç değerine etkisi araştırılmıştır. Her bir mineral katkı %0, %10, %20 ve %30 oranlarında çimento ile yer değiştirilerek farklı seriler tasarlanmıştır. Laboratuar ortamında beş yıl kür edilen harçların elektriksel özdirençleri iki plaka yöntemine göre belirlenmiştir. Elektriksel özdirenç değerleri 0.1, 0.12, 1, 10 ve 100 kHz olmak üzere farklı frekans değerleri için elde edilmiştir. Etüv kurusu harçlarda elde edilen elektriksel özdirenç sonuçlarına göre silis içeriği yüksek olan mineral katkıların kullanımı elektriksel özdirenç değerini düşürürken, kalsiyum oksit içeriği yüksek olan mineral katkıların kullanımı ile harçların özdirenç değerinin önemli derecede arttığı gözlenmiştir.