Standard oxidation-reduction reactions such as those of ferrocyanide and ferrocene have long been employed in evaluating and comparing new electrode structures with more traditional configurations. A variety of nanostructured carbon electrodes developed in recent years have been reported to exhibit faster electron transfer kinetics than more traditional carbon structures when studied with these redox reactions. This type of comparison has not been widely explored for nanostructured platinum electrodes that have become increasingly common. In this work, a platinum nanotubule array electrode was fabricated via a simple template-based process and evaluated using the standard ferrocyanide redox reaction. The nanotubule array electrodes were observed to more closely approach ideal reversible behavior than a typical Pt black/Nafion fuel cell electrode or a standard polished Pt disc electrode. The apparent heterogeneous electron transfer coefficient was determined using the Nicholson method and found to be one to two orders of magnitude greater for the nanotubule array electrodes, depending on the diameter of the nanotubules, in comparison with these same two more traditional electrode structures.

One-dimensional metallic nanostructures such as nanowires, rods, and tubes have drawn much attention for electrocatalytic applications due to potential advantages that include fewer diffusion impeding interfaces with polymeric binders, more facile pathways for electron transfer, and more effective exposure of active surface sites. 1D nanostructured electrodes have been fabricated using a variety of methods, typically showing improved current response which has been attributed to improved CO tolerance, enhanced surface activity, and/or improved transport characteristics. A template wetting approach was used to fabricate an array of platinum nanotubules which were examined electrochemically with regard to the electrooxidation of formic acid. Arrays of 100 and 200 nm nanotubules were compared to a traditional platinum black catalyst, all of which were found to have similar surface areas. Peak formic acid oxidation current was observed to be highest for the 100 nm nanotubule array, followed by the 200 nm array and the Pt black; however, CO tolerance of all electrodes was similar, as were the onset potentials of the oxidation and reduction peaks. The higher current response was attributed to enhanced mass transfer in the nanotubule electrodes, likely due to a combination of both the more open nanostructure as well as the lack of a polymeric binder in the catalyst layer.