The probiotic viability, physicochemical, mechanical, barrier, and microstructure properties of synbiotic edible films (SEFs) based on duck feet gelatin (DFG) were evaluated. Four synbiotic systems were obtained by mixing four types of prebiotics, namely, dextrin, polydextrose, gum Arabic, and sago starch, with DFG to immobilize of probiotic (Lactobacillus casei ATCC). The ability of DFG to create a suitable matrix to increase probiotic viability was compared with those of other commercial gelatins in a preliminary evaluation. The DFG showed proper probiotic viability compared with other gelatins. The addition of prebiotics reduced the transparency of SEFs and increased color differentiation, uniformity, and complete coverage of probiotic cells. The estimated shelf-life of surviving bacteria in the SEFs stored at 4 and 25 °C showed that gum arabic showed the best performance and enhanced the viability of L. casei by 42% and 45%, respectively. Dextrin, polydextrose, and sago starch enhanced the viability of L. casei at 4 and 25 °C by 26% and 35%, 26% and 5%, and 20% and 5%, respectively. The prebiotics improved the physicochemical, mechanical, and barrier properties of all SEFs, except polydextrose film. The viability of L. casei can be increased with the proper selection of gelatin and prebiotics.

This study aimed to describe the properties of cold water fish gelatin (FG) blended with poultry gelatin (PG) for a production of a sachet containing olive oil. To find a desirable film, the different ratio of FG-PG-based films were characterized in terms of mechanical properties. As the proportion of PG in PG-FG-based increased, the tensile strength and Young’s modulus were increased, and the elongation at break and heat seal strength of the films were decreased. The 50-50 film had favorable characteristics to use as a sachet. The amount of acid index and peroxide of the oil stored in the sachets after 14 days showed that there is a significant difference (p < 0.05) between the films. The barrier properties of the films including the water vapor permeability and oxygen permeability of films were increased from 1.21 to 4.95 × 10−11 g m−1 Pa−1 s−1 and 48 to 97 cm3 mµ/m2 d kPa, respectively. Dark, red, yellow, and opaque films were realized with increasing PG. Fourier transform infrared (FTIR) spectra approved a wide peak of approximately 2500 cm−1. The rheological analysis indicated that, by adding PG, viscosity, elastic modulus (G′) and loss modulus (G′′) were increased significantly (p < 0.05) about 9.5, 9.32 and 18 times, respectively. Therefore, an easy modification of FG with PG will make it suitable for oil sachet packaging applications for the food industry.