In this work the effect of thermal annealing treatment on the different physical, optical and structural of surgical suture fibers were considered. Polybutester monofilaments suture fibers were thermally annealed at temperatures fluctuating from 50-130? for two different periods of 60 and 120 min. The thermal-treatment was supported using taut end settings. Multiple-beam Fizeau fringes in transmission and X-ray diffraction techniques were used to measure the physical and structural properties of the tested sutures. Such as refractive indices, birefringence, dielectric constant, polarizability, dielectric susceptibility and the crystallinity. From the obtained measured data , there was a noticeable increase in the physical properties and crystallinity throughout the annealing process for annealing time 120 min. which indicates that a new reorientation of Novafil suture molecules was performed, which will improve the mechanical properties of the sutures. This is a significant enhancement for these suture fibers to broaden their medical use and improve their clinical results. The new molecular reorientation of the Novafil surgical sutures was performed using the annealing process which demonstrates the polymer-chain relaxation during the thermal annealing process. Micro Interferograms were used to illustrate these findings.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2025 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.