he bone tissue has a great regenerative potential, with ability to completely restore its structure and original functions. In some situations, though, bone defects cannot be self-repaired, thus requiring the use of grafts for a correct treatment and good prognosis. This work aimed at microscopically analyzing the effect of the particle size of demineralized bovine cancellous bone matrix in micro and macrogranular forms on the repair of bone defects in femurs of rabbits, with blood clot used as control. At 1, 3 and 6 months after implantation of the materials, the animals were killed and the anatomic specimens were removed. A foreign body-type granulomatous reaction containing macrophages and multinucleated giant cells in contact with the implanted particles was observed. These results suggest a failure in demineralization and/or interruption of the antigenic potential during production of the biomaterial. It is concluded that the size of the particles did not influence the evolution of the repair process of bone defects, acting only as bone-filler substances, and that the material implanted should be improved by quality control during production, since it may represent a good alternative for bone graft. Uniterms: Xenogenic graft; Bovine cancellous bone; Particle size; Femur; Rabbit. tecido ósseo possui grande potencial regenerativo com capacidade para restaurar completamente sua estrutura e função originais. Há situações em que os defeitos ósseos não conseguem por si só obter o reparo, casos em que se fazem necessários o uso de enxertos, para um correto tratamento e bom prognóstico. Este experimento teve o propósito de analisar microscopicamente o efeito do tamanho das partículas de matriz de osso medular bovino desmineralizado, nas formas micro e macrogranular, na reparação de defeito ósseo em fêmures de coelhos, tendo como controle o coágulo sanguíneo. Após 1,3 e 6 meses da implantação dos materiais, os animais foram mortos e as peças anatômicas removidas. Uma reação granulomatosa tipo corpo estranho, envolvendo as partículas implantadas, foi observada. Estes resultados sugerem falhas na desmineralização e/ou na retirada de potenciais antigênicos durante a produção do biomaterial. Podemos concluir que o tamanho das partículas não influenciou na evolução do processo reparativo dos defeitos ósseos, atuando apenas como substâncias osteopreenchedoras e que o material implantado deverá sofrer um aprimoramento no controle de qualidade na linha de produção, uma vez que poderá representar uma boa alternativa para enxertos ósseos. Unitermos: Enxerto xenogênico; Osso medular bovino; Tamanho de partícula; Fêmur; Coelhos. 2005; 13(2): 157-62 J Appl Oral Sci

C Considering previous studies on the similarity between the chemical composition of the mineral trioxide aggregate and the Portland cement, the purpose of this study was to investigate the pulp response of dog's teeth after pulpotomy and direct pulp protection with MTA Angelus and white Portland cement. Thirty eight pulp remnants were protected with these materials. One hundred and twenty days after treatment, the animals were sacrificed and the specimens removed and prepared for histological analysis. Both materials demonstrated the same results when used as pulp capping materials, inducing hard tissue bridge formation and maintaining pulp vitality in all specimens. The MTA Angelus and the white Portland cement showed to be effective as pulp protection materials following pulpotomy. UNITERMS: Pulpotomy; Mineral trioxide aggregate; White Portland cement.onsiderando estudos anteriores sobre a similaridade entre a composição química do agregado de trióxido mineral e o cimento Portland, o objetivo deste estudo foi investigar a resposta pulpar de dentes de cães após pulpotomia e proteção pulpar direta com MTA Angelus e cimento Portland branco. Trinta e oito remanescentes pulpares foram recobertos com esses materiais. Cento e vinte dias após o tratamento, os animais foram sacrificados e os espécimes removidos e preparados para análise histológica. Ambos os materiais demonstraram os mesmos resultados quando utilizados como materiais de capeamento pulpar, induzindo a formação de ponte de tecido mineralizado e mantendo a vitalidade pulpar em todos os espécimes. Ambos matérias se mostraram efetivos como protetores pulpares após pulpotomia em dentes de cães. UNITERMOS: Pulpotomia; MTA; Cimento Portland branco.www.fob.usp.br -www.scielo.br ABSTRACT RESUMO

The objective of this study was to evaluate the influence of calcium hydroxide in intracanal dressing on the ability of the dyes rhodamine B and methylene blue to label the dentine. Forty extracted human mandibular premolars had their canals instrumented and were divided into four groups: in two groups, the canals were filled with a calcium hydroxide paste and the others remained in distilled water. After 15 days, in two groups (with and without dressing), the canals were obturated with sealer containing methylene blue, whereas the others contained rhodamine B. For analysis, the roots were transversally sectioned in their cervical, medium and apical thirds, and the labeling was analyzed. The Mann-Whitney test showed statistically significant difference between the dressing/methylene blue group and the others. Based on these results, it was concluded that calcium hydroxide in intracanal dressing negatively interferes with the labeling ability of methylene blue.