Maraging steels are generally characterized by excellent mechanical properties, which make them ideal for various industrial applications. The application field can be further extended by using selective laser melting (SLM) for additive manufacturing of shape complicated products. However, the final mechanical properties are strongly related to the microstructure conditions. The present work studies the effect of heat treatment on the microstructure and mechanical properties of 3D printed samples prepared from powder of high-strength X3NiCoMoTi 18-9-5 maraging steel. It was found that the as-printed material had quite low mechanical properties. After sufficient heat treatment, the hardness of the material increased from 350 to 620 HV0.1 and the tensile yield strength increased from 1000 MPa up to 2000 MPa. In addition, 3% ductility was maintained. This behavior was primarily affected by strong precipitation during processing.

Fe–Al–Si alloys have been previously reported as an interesting alternative to common high-temperature materials. This work aimed to improve the properties of FeAl20Si20 alloy (in wt.%) by the application of powder metallurgy process consisting of ultrahigh-energy mechanical alloying and spark plasma sintering. The material consisted of Fe3Si, FeSi, and Fe3Al2Si3 phases. It was found that the alloy exhibits an anomalous behaviour of yield strength and ultimate compressive strength around 500 °C, reaching approximately 1100 and 1500 MPa, respectively. The results also demonstrated exceptional wear resistance, oxidation resistance, and corrosion resistance in water-based electrolytes. The tested manufacturing process enabled the fracture toughness to be increased ca. 10 times compared to the cast alloy of the same composition. Due to its unique properties, the material could be applicable in the automotive industry for the manufacture of exhaust valves, for wear parts, and probably as a material for selected aggressive chemical environments.

No abstract

Fe-Al-Si alloys have been recently developed in order to obtain excellent high-temperature mechanical properties and oxidation resistance. However, their production by conventional metallurgical processes is problematic. In this work, an innovative processing method, based on ultra-high energy mechanical alloying, has been tested for the preparation of these alloys. It has been found that the powders of low-silicon alloys (up to 10 wt. %) consist of FeAl phase supersaturated by Si after mechanical alloying. Fe2Al5 phase forms as a transient phase at the initial stage of mechanical alloying. The alloy containing 20 wt. % of Si and 20 wt. % of Al is composed mostly of iron silicides (Fe3Si and FeSi) and FeAl ordered phase. Thermal stability of the mechanically alloyed powders was studied in order to predict the sintering behavior during possible compaction via spark plasma sintering or other methods. The formation of Fe2Al5 phase and Fe3Si or Fe2Al3Si3 phases was detected after annealing depending on the alloy composition. It implies that the powders after mechanical alloying are in a metastable state; therefore, chemical reactions can be expected in the powders during sintering.