Modern ultrashort pulse lasers with scanning systems provide a huge set of parameters affecting the suitability for dental applications. The present study investigates thresholds and ablation rates of oral hard tissues and restorative materials with a view towards a clinical application system. The functional system consists of a 10 W Nd:YVO4 laser emitting pulses with a duration of 8 ps at 1,064 nm. Measurements were performed on dentin, enamel, ceramic, composite, and mammoth ivory at a repetition rate of 500 kHz. By employing a scanning system, square-shaped cavities with an edge length of 1 mm were created. Ablation threshold and rate measurements were assessed by variation of the applied fluence. Examinations were carried out employing a scanning electron microscope and optical profilometer. Irradiation time was recorded by the scanner software in order to calculate the overall ablated volume per time. First high power ablation rate measurements were performed employing a laser source with up to 50 W. Threshold values in the range of 0.45 J/cm(2) (composite) to 1.54 J/cm(2) (enamel) were observed. Differences between any two materials are statistically significant (p < 0.05). Preparation speeds up to 37.53 mm(3)/min (composite) were achieved with the 10 W laser source and differed statistically significant for any two materials (p < 0.05) with the exception of dentin and mammoth ivory (p > 0.05). By employing the 50 W laser source, increased rates up to ∼50 mm(3)/min for dentin were obtained. The results indicate that modern USPL systems provide sufficient ablation rates to be seen as a promising technology for dental applications.

Heat generation during the removal of dental hard tissues may lead to a temperature increase and cause painful sensations or damage dental tissues. The aim of this study was to assess heat generation in dental hard tissues following laser ablation using an ultrashort pulse laser (USPL) system. A total of 85 specimens of dental hard tissues were used, comprising 45 specimens of human dentine evaluating a thickness of 1, 2, and 3 mm (15 samples each) and 40 specimens of human enamel with a thickness of 1 and 2 mm (20 samples each). Ablation was performed with an Nd:YVO4 laser at 1,064 nm, a pulse duration of 9 ps, and a repetition rate of 500 kHz with an average output power of 6 W. Specimens were irradiated for 0.8 s. Employing a scanner system, rectangular cavities of 1-mm edge length were generated. A temperature sensor was placed at the back of the specimens, recording the temperature during the ablation process. All measurements were made employing a heat-conductive paste without any additional cooling or spray. Heat generation during laser ablation depended on the dental hard tissue (enamel or dentine) and the thickness of the respective tissue (p < 0.05). Highest temperature increase could be observed in the 1-mm thickness group for enamel. Evaluating the 1-mm group for dentine, a significantly lower temperature increase could be measured (p < 0.05) with lowest values in the 3-mm group (p < 0.05). A time delay for temperature increase during the ablation process depending on the material thickness was observed for both hard tissues (p < 0.05). Employing the USPL system to remove dental hard tissues, heat generation has to be considered. Especially during laser ablation next to pulpal tissues, painful sensations and potential thermal injury of pulp tissue might occur.

Ultrashort pulsed lasers (USPLs) represent a new generation of laser systems in the field of biophotonical applications. In terms of a pilot project, the study was carried out to evaluate the ablation parameters of bone tissue regarding the medical use of such a laser technology in dentistry. Specimens from ribs of freshly slaughtered pigs were assembled and irradiated with an USP Nd:YVO4 laser (pulse duration 8 ps at 1,064 nm with repetition rates between 50 and 500 kHz) using eligible average output powers in the range of 3.5-9 W and fluences between 1 and 2.5 J/cm(2). Square-shaped cavities of 1-mm edge length in the bone compacta were created employing a scanner system. Cavities were analyzed with an optical profilometer to determine the ablated volume. Ablation rate was calculated by the ablated volume and the recorded irradiation time by the scanner software. Additionally, samples were examined histologically to investigate side effects of the surrounding tissue. Formed cavities showed a precise and sharp-edged appearance in bone compacta. Optimized ablation rate of 5.2 mm(3)/min without any accompanying side effects was obtained with an average output power of 9 W, a pulse repetition rate of 500 kHz, and an applied fluence of 2.5 J/cm(2). Provided that the used laser system will be advanced and adjusted for clinical applications, the outcome of this study shows auspicious possibilities for the use of USPL systems in the preparation of bone tissue.

Heat generation during the removal of dental restorative materials may lead to a temperature increase and cause painful sensations or damage dental tissues. The aim of this study was to assess heat generation in dental restoration materials following laser ablation using an ultrashort pulse laser (USPL) system. A total of 225 specimens of phosphate cement (PC), ceramic (CE), and composite (C) were used, evaluating a thickness of 1 to 5 mm each. Ablation was performed with an Nd:YVO(4) laser at 1,064 nm, a pulse length of 8 ps, and a repetition rate of 500 kHz with a power of 6 W. Employing a scanner system, rectangular cavities of 1.5-mm edge length were generated. A temperature sensor was placed at the back of the specimens to record the temperature during the ablation process. All measurements were made employing a heat-conductive paste without any additional cooling or spray. Heat generation during laser ablation depended on the thickness of the restoration material (p < 0.05) with the highest values in the composite group (p < 0.05), showing an increase of up to 17 K. A time delay for temperature increase during the ablation process depending on the material thickness was observed in the PC and C group (p < 0.05) with highest values for cement (p < 0.05). Employing the USPL system for removal of restorative materials, heat generation has to be considered. Especially during laser ablation next to pulpal tissues, painful sensations might occur.

No abstract