Three different types of mixed-oxides ceramic ball heads have been investigated for their wear behaviour against acetabular cups of the same materials in a hip joint simulator. Mixed-oxides ceramics have been indicated in literature as a promising compromise between strength and wear but no reports are available on the influence of a percentage of zirconia in a ceramic femoral head when sliding against itself. Mixed-oxides ceramic acetabular cups and femoral heads were tested on a simulator apparatus with a sinusoidal load in presence of bovine calf serum. The experimental results did not show any significant difference between the experimental and commercial ceramic material couplings. These results were found to be in accord with those developed in Part 1.

No abstract

No abstract

No abstract

A fracture of a ceramic femoral head is reported in this study. Fractures of ceramic femoral heads are uncommon and reports on this complication are rare. After 3 million cycles, on a twelve station hip simulator that tested alumina femoral head against polyethylene acetabular cup, fracture of the ceramic ball was observed. The retrieved specimen consisted of three large ceramic fragments from the same ceramic femoral head, a polyethylene acetabular cup and a stainless steel jig. Careful and detailed examination of the removed components was made. The fracture of the ceramic ball resulted in damage to the metal taper of the jig component which was fixed into the simulator.