No abstract

No abstract

Objective: The purpose of this study was to evaluate the dimensions and surface characteristics of orthodontic wires and bracket slots of different commercial brands. Methods: Thirty metallic brackets (0.022 x 0.028-in and 0.022 x 0.030-in) were divided in three groups: DYN/3M group = Dyna-Lock, 3M/Unitek (stainless steel, or SS); STD/MO group = Slim Morelli (SS); and Ni-Free/MO group = Slim Morelli (Ni-Free). The stainless steel wires (0.019 x 0.025-in) were divided into two groups: MO group = Morelli; and 3M group = 3M/Unitek. The bracket and wire measurements were done by two methods: (a) Surface Electron Microscopy (SEM), and (b) Profile projection. The surface analysis was done qualitatively, based on SEM images and/or by a rugosimeter. The quantitative results were analyzed by ANOVA with Tukey's test (p < 0.05) and Student's t test. Results: A significant difference in the dimensions of slots was observed, and the NiFree/MO group showed the greatest changes when compared to the other groups. The analysis of surface topography of the brackets indicated greater homogeneity of the metallic matrix for DYN/3M and STD/MO groups. As for the dimensions of the wires, groups showed statistically different mean heights. Conclusions: It was concluded that wires and brackets slots can present altered dimensions, which might directly and unintentionally affect the planned tooth movement.Keywords: Orthodontic brackets. Orthodontic wires. Friction.Objetivo: o objetivo desse estudo é avaliar as dimensões e as características superficiais de fios retangulares e slots de braquetes de diferentes marcas comerciais. Métodos: trinta braquetes metálicos (0,022" x 0,028'' e 0,022'' x 0,030'') foram divididos em três grupos: Grupo DYN/3M = Dyna-Lock, 3M/Unitek, aço inoxidável (AI); Grupo STD/MO = Slim Morelli (AI); e Grupo NiFree/MO = Slim Morelli (Ni-Free). Já os fios retangulares (0,019" x 0,025''), de aço inoxidável, foram divididos em 2 grupos: Grupo MO = Morelli; Grupo 3M = 3M/Unitek. As mensurações dos slots dos braquetes e dos fios foram realizadas por dois métodos: (a) microscopia eletrônica de varredura (MEV), e (b) projeção de perfil. A análise da topografia superficial foi realizada qualitativamente, baseada em imagens microscópicas (MEV) e/ou por meio de um rugosímetro. Os resultados quantitativos foram submetidos à análise de variância (ANO-VA) com o teste de Tukey (p < 0,05) ou o teste t de Student. Resultados: observou-se diferença significativa entre as dimensões dos slots dos braquetes, sendo que o Grupo NiFree/MO apresentou a maior alteração quando comparado aos demais Grupos. A análise da topografia superficial dos braquetes indicou maior homogeneidade da matriz metálica nos Grupos DYN/3M e STD/MO. Quanto às dimensões dos fios, os grupos tiveram alturas médias estatisticamente diferentes entre si. Conclusão: concluiu-se que a conformação dos fios e dos slots dos braquetes pode apresentar alterações dimensionais, o que afetará direta e indesejavelmente o movimento dentário planejado.Palavras-chave: Braquetes ortod...

Objectives: The purpose of this study was to analyze, with the aid of scanning electron microscopy (SEM), the chemical and structural changes in metal brackets subjected to an in vitro biodegradation process. Methods: The sample was divided into three groups according to brackets commercial brand names, i.e., Group A = Dyna-Lock, 3M/Unitek (AISI 303) and Group B = LG standard edgewise, American Orthodontics (AISI 316L). The specimens were simulated orthodontic appliances, which remained immersed in saline solution (0.05%) for a period of 60 days at 37°C under agitation. The changes resulting from exposure of the brackets to the saline solution were investigated by microscopic observation (SEM) and chemical composition analysis (EDX), performed before and after the immersion period (T0 and T5, respectively). Results: The results showed, at T5, the formation of products of corrosion on the surface of the brackets, especially in Group A. In addition, there were changes in the composition of the bracket alloy in both groups, whereas in group A there was a reduction in iron and chromium ions, and in Group B a reduction in chromium ions. Conclusions: The brackets in Group A were less resistant to in vitro biodegradation, which might be associated with the type of steel used by the manufacturer (AISI 303). Editor's summaryThe occurrence of hypersensitivity caused by the nickel present in stainless steel alloyswidely used in orthodontic treatment-has become increasingly common. Orthodontic brackets, bands and archwires are universally made from this alloy, which contains about 6% to 12% nickel and 15% to 22% chromium. Besides allergenicity, carcinogenic, mutagenic and cytotoxic effects have been attributed to nickel and, to a lesser extent, chromium. One of the factors that determine the biocompatibility of alloys used in dentistry is their resistance to corrosion. However, despite the high resistance of austenitic stainless steel-the major alloy employed in the manufacture of orthodontic brackets-several studies have revealed the corrosion of these brackets. In view of the wide array of factors associated with * Access www.dentalpress.com.br/journal to read the full article.

OBJETIVO: comparar a resistência ao cisalhamento de cinco materiais utilizados na cimentação de bandas ortodônticas: um cimento de ionômero de vidro convencional (Ketac Cem), dois cimentos de ionômero de vidro modificados por resina (3M Multicure Glass Ionomer Cement e Fuji Ortho LC) e duas resinas compostas modificadas por poliácidos (Ultra Band-Lok e Transbond Plus). METODOLOGIA: sobre a superfície de um segmento de banda (6 x 6mm) foi posicionada uma matriz com um orifício de 3mm de diâmetro na qual foi inserido o material para cimentação. Metade da amostra foi jateada com partículas de óxido de alumínio. Os corpos-de-prova foram armazenados a 37ºC por 24 horas em umidade relativa de 100% e submetidos ao teste de cisalhamento a uma velocidade de 0,5mm/min. Utilizou-se ANOVA e o teste de comparações múltiplas de Tukey para comparar os grupos em cada tipo de superfície estudada (com ou sem jateamento), e o teste t Student para amostras pareadas para a comparação dos grupos jateados e não-jateados (p=0,01). RESULTADOS: nos grupos não-jateados, Ultra Band-Lok apresentou uma resistência de união significativamente maior (p<0,01) que a obtida pelos outros materiais, os quais não apresentaram diferença significante entre si. Após o jateamento, as resinas compostas modificadas por poliácidos apresentaram uma resistência de união significativamente maior (p<0,01) que a obtida pelos demais cimentos, sendo que 3M Multicure Glass Ionomer apresentou um valor de união superior (p<0,01) ao obtido pelo Ketac Cem e Fuji Ortho LC. CONCLUSÃO: o jateamento aumentou significativamente (p<0,01) a resistência de união em todos os grupos.