Mechanical loading plays a critical role in cardiac pathophysiology. Engineered heart tissues derived from human induced pluripotent stem cells (iPSCs) allow rigorous investigations of the molecular and pathophysiological consequences of mechanical cues. However, many engineered heart muscle models have complex fabrication processes and require large cell numbers, making it difficult to use them together with iPSC-derived cardiomyocytes to study the influence of mechanical loading on pharmacology and genotype–phenotype relationships. To address this challenge, simple and scalable iPSC-derived micro-heart-muscle arrays (μHM) have been developed. “Dog-bone-shaped” molds define the boundary conditions for tissue formation. Here, we extend the μHM model by forming these tissues on elastomeric substrates with stiffnesses spanning from 5 to 30 kPa. Tissue assembly was achieved by covalently grafting fibronectin to the substrate. Compared to μHM formed on plastic, elastomer-grafted μHM exhibited a similar gross morphology, sarcomere assembly, and tissue alignment. When these tissues were formed on substrates with different elasticity, we observed marked shifts in contractility. Increased contractility was correlated with increases in calcium flux and a slight increase in cell size. This afterload-enhanced μHM system enables mechanical control of μHM and real-time tissue traction force microscopy for cardiac physiology measurements, providing a dynamic tool for studying pathophysiology and pharmacology.

Micro-fibrillated cellulose (MFC) derived from natural fibre is continuously gaining interest to produce an environmentally-friendly material, due to economic and ecological reasons. In consequence, sorghum is one of the most-cultivated crops that usually remain the waste as by product of bioethanol production. Indeed, it will be a promising area to utilize sorghum waste to produce MFC for enhancing polymer performance, especially in terms of crystallinity. The objective of this study is to investigate the effect of a sequence of chemical modification was applied to sorghum fibres, i.e. alkalization using 4% sodium hydroxide followed by bleaching using 1.7% sodium chlorite plus acetic acid as a buffer. The treatment was purposed to unbundle the lignocellulose networks into microfibrils cellulose with less amorphous part and lower hydrophilic properties. Evaluation of the chemical treatments effect on internal microstructure, crystallinity index and chemical composition of sorghum fibre was measured via Field-Emission Scanning Electron microscope (FE-SEM), X-ray Diffraction (XRD) and Fourier Transformation Infra-Red (FTIR) Spectroscopy. The experiments show that treatments led to a removal of binding materials, such as amorphous parts hemicellulose and lignin, from the sorghum fibres, resulting MFC of sorghum fibres and enhanced crystallinity index from 41.12 % to 75.73%.

Transparent conductive oxide (TCO) glass is one of most important components in dyesensitized solar cell (DSSC) device. In addition to its high electrical conductivity, transparency is another important requirement that must be achieved in fabricating TCO. One TCO film is fluorine-doped tin oxide (FTO), which can be considered as the most promising substitution for indium-doped tin oxide (ITO), since the latter is very expensive. However, the fabrication techniques for TCO film need to be carefully selected; the synthesis parameters must be properly optimized to provide the desired properties. In this work, FTO glass has been fabricated by the ultrasonic spray pyrolisis technique with different precursors, i.e. tin (II) chloride dihydrate (SnCl 2 .2H 2 O) and anhydrous tin (IV) chloride (SnCl 4 ), as well as different solvents, i.e. ethanol and methanol. For both conditions, ammonium fluoride (NH 4 F) was used as the doping compound. The resulting thin films were characterized by use of a scanning electron microscope (SEM), x-ray diffraction (XRD), ultraviolet-visible (UV-Vis) spectroscopy and a four-point probe test. The results of the investigation show that the highest transmittance of 88.3% and the lowest electrical resistivity of 8.44×10 -5 Ω.cm were obtained with the FTO glass processed with 20 minutes of spray pyrolysis deposition and 300 o C substrate heating, using SnCl 4 as the precursor and methanol as the solvent. It can be concluded that TCO fabrication with tin chloride precursors and ammonium fluoride doping using ultrasonic spray pyrolisis can be considered as a simple and low cost method, as well as a breakthrough in manufacturing conductive and transparent glass.

Tissue-engineered in vitro models are an essential tool in biomedical research. Tissue geometry is a key determinant of function, but controlling the geometry of microscale tissues remains challenging. Additive manufacturing approaches have emerged as a promising means for rapid and iterative changes in the geometry of microdevices. However, it has been shown that poly(dimethylsiloxane) (PDMS) cross-linking is often inhibited at the interface of materials printed with stereolithography. While approaches to replica mold stereolithographic three-dimensional (3D) prints have been described, these methods are inconsistent and often lead to print destruction when unsuccessful. Additionally, 3D-printed materials often leach toxic chemicals into directly molded PDMS. Here, we developed a double molding approach that allows precise replication of high-resolution stereolithographic prints into poly(dimethylsiloxane) (PDMS) elastomer, facilitating rapid design iterations and highly parallelized sample production. Inspired by lost wax casting, we used hydrogels as intermediary molds to transfer high-resolution features from high-resolution 3D prints into PDMS, while previously published work focused on enabling direct molding of PDMS onto 3D prints through the use of coatings and post-crosslinking treatments of the 3D print itself. Hydrogel mechanical properties, including cross-link density, predict replication fidelity. We demonstrate the ability of this approach to replicate a variety of shapes that would be impossible to create using photolithography techniques traditionally used to create engineered tissue designs. This method also enabled the replication of 3D-printed features into PDMS that would not be possible with direct molding as the stiffness of these materials leads to material fracture when unmolding, while the increased toughness in the hydrogels can elastically deform around complex features and maintain replication fidelity. Finally, we highlight the ability of this method to minimize the potential for toxic materials to transfer from the original 3D print into the PDMS replica, enhancing its use for biological applications. This minimization of the transfer of toxic materials has not been reported in other previously reported methods describing replication of 3D prints into PDMS, and we demonstrate its use through the creation of stem cell-derived microheart muscles. This method can also be used in future studies to understand the effects of geometry on engineered tissues and their constitutive cells.