In this study, spent activated carbons (ACs) were collected from a waste water treatment plant (WWTP) in Incheon, South Korea, and regenerated by heat treatment and KOH chemical activation. The specific surface area of spent AC was 680 m2/g, and increased up to 710 m2/g through heat treatment. When the spent AC was activated by the chemical agent potassium hydroxide (KOH), the surface area increased to 1380 m2/g. The chemically activated ACs were also washed with acetic acid (CH3COOH) to compare the effect of ash removal during KOH activation. The low temperature N2 adsorption was utilized to measure the specific surface areas and pore size distributions of regenerated ACs by heat treatment and chemical activation. The functional groups and adsorbed materials on ACs were also analyzed by X-ray photoelectron spectroscopy and X-ray fluorescence. The generated ash was confirmed by proximate analysis and elementary analysis. The regenerated ACs were tested for toluene adsorption, and their capacities were compared with commercial ACs. The toluene adsorption capacity of regenerated ACs was higher than commercial ACs. Therefore, it is a research to create high value-added products using the waste.

In this study, a feasible experiment on adsorbed natural gas (ANG) was performed using activated carbons (ACs) with high surface areas. Upgraded ACs were prepared using chemical activation with potassium hydroxide, and were then applied as adsorbents for methane (CH4) storage. This study had three principal objectives: (i) upgrade ACs with high surface areas; (ii) evaluate the factors regulating CH4 adsorption capacity; and (iii) assess discharge conditions for the delivery of CH4. The results showed that upgraded ACs with surface areas of 3052 m2/g had the highest CH4 storage capacity (0.32 g-CH4/g-ACs at 3.5 MPa), which was over two times higher than the surface area and storage capacity of low-grade ACs (surface area = 1152 m2/g, 0.10 g-CH4/g-ACs). Among the factors such as surface area, packing density, and heat of adsorption in the ANG system, the heat of adsorption played an important role in controlling CH4 adsorption. The released heat also affected the CH4 storage and enhanced available applications. During the discharge of gas from the ANG system, the residual amount of CH4 increased as the temperature decreased. The amount of delivered gas was confirmed using different evacuation flow rates at 0.4 MPa, and the highest efficiency of delivery was 98% at 0.1 L/min. The results of this research strongly suggested that the heat of adsorption should be controlled by both recharging and discharging processes to prevent rapid temperature change in the adsorbent bed.

No abstract

Spent activated carbon (SAC) usually exhibits a low specific surface area due to its high ash contents. In this study, pre-treatments, such as heat and acid treatments, were optimized to improve this feature. The heat pre-treatment did not reduce the ash content, nor did it increase the surface area. Because metallic ions adsorbed in SACs turn into ash upon the heat treatment. In the acid pre-treatment, the volatiles and fixed carbon were increased with decreasing ash contents. In this study, it was found that the surface area increase was correlated with the ratio between fixed carbon and ash. Among the pre-treatment methods, the combined heat and acid pre-treatment method highly increased the ratio, and therefore led to the surface area increase. Additionally, the acid pre-treatment was carried out using different types of acid (organic and inorganic acids) solutions to further improve the surface areas. The organic acid treatment caused a significant structural collapse compared to the inorganic acid treatment, decreasing the surface area. In particular, H3PO4 effectively removed ashes adsorbed on the activated carbon surface and regenerated the exhausted activated carbon. Both the heat and acid pre-treatments before chemical activation resulted in the positive effects such as strong desorption of pollutants and ashes within the internal structure of the activated carbon. Therefore, the regeneration introduced in this study is methodically the best method to regenerate SAC and maintain a stable structure.

This study was a preliminary investigation of solid recovered fuel production from spent coffee grounds using the hydrothermal carbonization (HTC) technique. The spent coffee grounds (SCGs) were subjected to HTC at 170 to 250 °C. The biochar was characterized by proximate analysis, ultimate analysis, capillary suction time, time to filter, suspended solids, and particle size distribution. The biochar yields decreased with increasing HTC temperature and time. However, the higher heating value (HHV) of biochar increased with the HTC temperature and time. The H/C slop relative to the O/C atomic rate of spent coffee grounds was 0.10 with low decarboxylation selectivity. Considering the HHV of biochar and dehydration capacity depend on ratio of H/C vs. O/C, the optimum reaction temperature of HTC was 200 °C, and the biochar from SCGs is an attractive biochar.