In this work, the structural and magnetic properties of the polycrystalline La 0.85 Ag 0.15 MnO 3 (LAM) and (La 0.80 Pr 0.20 ) 0.85 Ag 0.15 MnO 3 (LPAM) compounds prepared by the sol-gel method were investigated. The structural properties of both polycrystalline compounds were investigated by X-ray diffraction (XRD), scanning electron microscope (SEM), and energy dispersive X-ray spectrum (EDX) methods. The XRD results showed that both samples crystallized in the hexagonal symmetry with R3c space group. The SEM images showed that the particles are closely packed with each other, and their size range from 0.5 to 2.0 μm with the average sizes of 1.23 and 1.03 μm, for LAM and LPAM, respectively. From the EDX spectrum, in both compounds, we did not see loss of any integrated elements during the sintering process and no other impurity elements. The magnetic properties were studied by employing temperature M(T ) and external magnetic field M(H ) dependence of magnetization measurements. Both compounds showed magnetic phase transition from paramagnetic to ferromagnetic phase. With the substitution of Pr for La, the Curie temperature, T C , decreased from 262 to 216 K. At a field change of 5 T, LAM and LPAM showed large magnetic entropy changes of 7.90 and 4.96 J kg −1 K −1 , respectively. Furthermore, their relative cooling power (RCP) values were found as 213.32 and .02 J kg −1 , respectively. These findings make both LAM and LPAM compounds as good candidates for the practical magnetic refrigeration.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.