1High-temperature corrosion fatigue, a combination of corrosion with a fatigue cycle, is an emerging generic issue affecting power generation and aero gas turbine engines and has the potential to limit component life. Historically, surface treatments, such as shot peening have been used to improve component life and have been optimised for fatigue response. Research into optimisation of shot peening techniques for hot corrosion and high-temperature corrosion fatigue has shown 6-8A 230H 200% coverage to provide overall optimum performance for nickel-based superalloy 720Li based on the limited data within this study. Utilisation of electron backscatter diffraction techniques, in combination with detailed assessment of corrosion products have been undertaken as part of this work. The resultant cold-work visualisation technique provides a novel method of determining the variation in material properties due to the shot peening process and the interaction with hot corrosion. Through this work it has been shown that all three shot peening outputs must be considered to minimise the effect of corrosion fatigue, the cold work, residual stress and surface roughness. Further opportunity for optimisation has also been identified based on this work.

This is a PDF file of an article that has undergone enhancements after acceptance, such as the addition of a cover page and metadata, and formatting for readability, but it is not yet the definitive version of record. This version will undergo additional copyediting, typesetting and review before it is published in its final form, but we are providing this version to give early visibility of the article. Please note that, during the production process, errors may be discovered which could affect the content, and all legal disclaimers that apply to the journal pertain.

No abstract

Abstract. The nickel based superalloy 720Li is employed in the gas turbine due to its mechanical performance at elevated temperature. A comprehensive assessment of the materials behaviour under representative service conditions is reported to address the drive for ever increasing temperatures and more arduous environmental exposure. Fatigue experiments have been performed in an air and air/SO x environment at 700• C containing a mixed salt as a contaminant. There is an intimate relationship between local salt level (flux), stress level and stress state, i.e. static or cyclic. The interaction with these variables with the work hardened layer present on the surface of all tested specimens as a result of the shot peening process directly affects the crack initiation process. If specific conditions of environment and stress are achieved, a significant reduction in fatigue life is observed.

No abstract