Abstract:Aim:Evaluate surface treatments and silane application methods and their effect on shear bond strength (SBS) before and after aging. Materials and methods. Slices of IPS e.max CAD and Vitablocs Mark II, were embedded in acrylic resin. The block was randomly assigned to 5 groups; E:etching with hydrofluoric acid (HF), rinsing, followed by cleaning in ultrasonic bath; E/S:HFetching and cleaned as group E followed by silane application for 20s, air drying and hot drying; E/S+:HFetching and cleaned as group E, followed by silane application for 60s, air drying and hot air drying, rinsing with boiling water and hot air drying; S:silane application for 20s followed by air drying and hot air drying; S+:silane application for 60s followed by air drying, air drying and hot air drying, rinsing in boiling water and hot drying. Cylinders of composite resin (n=12) were bonded with adhesive. SBS testing was carried out after 24h or after thermocycling for groups E; E/S and E/S+. Results. For 24h SBS showed sign

Abstract:Aim:Evaluate surface treatments and silane application methods and their effect on shear bond strength (SBS) before and after aging. Materials and methods. Slices of IPS e.max CAD and Vitablocs Mark II, were embedded in acrylic resin. The block was randomly assigned to 5 groups; E:etching with hydrofluoric acid (HF), rinsing, followed by cleaning in ultrasonic bath; E/S:HFetching and cleaned as group E followed by silane application for 20s, air drying and hot drying; E/S+:HFetching and cleaned as group E, followed by silane application for 60s, air drying and hot air drying, rinsing with boiling water and hot air drying; S:silane application for 20s followed by air drying and hot air drying; S+:silane application for 60s followed by air drying, air drying and hot air drying, rinsing in boiling water and hot drying. Cylinders of composite resin (n=12) were bonded with adhesive. SBS testing was carried out after 24h or after thermocycling for groups E; E/S and E/S+. Results. For 24h SBS showed sign