Abstract. In order to investigate the influence of different shot peenings on the rolling contact fatigue life of case−hardened steel, the thrust type rolling contact fatigue test was performed with a ball−on−disk contact tester. In this study, the case−hardened steel disks were treated by the fine particle peening with a shot diameter of 0.05 mm and the normal shot peening with a shot diameter of 0.30 mm. The surface hardness and the surface compressive residual stress of the test disks were increased by these peenings. On the other hand, the surface roughness of the test disks was increased by the normal shot peening, and was decreased by the fine particle peening. The rolling contact fatigue test showed that the rolling contact fatigue life of the test disks was improved by the fine particle peening, and was not improved by the normal shot peening. The rolling contact fatigue life of the test disks became longer as their surface roughness became smaller. Therefore, it follows from this that the fine particle peening, which can provide the increase in surface hardness and the decrease in surface roughness, is good for the increase in the rolling contact fatigue life of case−hardened steel.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.