Novel co‐polymerization polyimide (PI) fibers based on 4,4′‐oxydianiline (ODA)‐pyromellitic dianhydride (PMDA) were prepared. 2‐(4‐Aminophenyl)‐5‐aminobenzimidazole (PABZ) containing the NH group was introduced into the structure of the fibers as the proton donor. The results of Fourier transform infrared (FTIR) and dynamic mechanical analysis (DMA) showed that hydrogen bonding occured between the NH group and chains, which strongly enhanced interchain interaction. This hydrogen bonding interaction increased the tensile strength and initial modulus of the PI fibers up to 2.5 times and 26 times, respectively, compared to those of homo‐PI PMDA‐ODA fibers with no hydrogen‐bonding interaction because of the absence of proton donors after the imidization process. In the mean time, glass transition temperature (Tg) of the modified PI fibers was found to be 410–440°C, which was higher than that of the homo‐PI PMDA‐ODA fibers. From the result, a novel access to molecular design and manufacture of high performance PI fibers with good properties could be provided. Copyright © 2009 John Wiley & Sons, Ltd.

A series of random copolyamic acid were synthesized from various ratios of two diamines 4, 4′‐oxydianiline (ODA) and 2‐(4‐aminophenyl)‐5‐aminobenzimidazole (PABZ) by polycondensation with pyromellitic dianhydride (PMDA) in N‐methyl‐2‐pyrrolidone (NMP). Their inherent viscosities were in the range of 1.89–2.91 dl/g. The polyamic acid (PAA) solution drops were spun into fibers by the wet spinning process. The polyimide (PI) fibers were obtained from PAA fibers after drawn and treated in heating tube. The fibers were characterized by fourier transform infrared (FTIR), wide X‐ray diffraction (WAXD), scanning electron microscope (SEM), thermal gravimetry analysis (TGA), dynamic mechanical analysis (DMA), and tensile testing. WAXD showed these PI fibers were basically amorphous. The tensile strength and initial modulus of the PI fiber reached 1.53 and 220.5 GPa when diamine ratio of PABZ/ODA was 7/3, which were almost three times and 30 times over that of the PMDA/ODA PI fibers. TGA showed that the PI fibers were thermally stable with 10% weight losses recorded in the range of 492–564°C under nitrogen atmosphere, and their glass transition temperature (Tg) were found to be 410–440°C by DMA with increasing PABZ content from 30 to 70%. POLYM. ENG. SCI., 2008. © 2008 Society of Plastics Engineers

No abstract

No abstract