Introduction The radial head has an ellipsoid shape so that a longest and a shortest axis can be defined. The aim of this study is to evaluate the position of the longest axis of the radial head (LARH) in relation to proximal radioulnar joint (PRUJ) and to the forearm in neutral position using 3D computed tomography (CT). Materials and methods 3D CT reconstructions of the distal humerus, the radius and the ulna of 27 healthy volunteers (average age 27.65 ± 9.25; 24 males, 3 females) were created. First an evaluation of the elliptic form of the radial head and the location of its longest axis was performed. Next, three planes were defined: the PRUJ plane, the forearm plane and a neutral plane. Based on the angle between the forearm plane and the neutral plane, the rotation of the scanned forearm was measured. Taking this rotation into account, the position of the LARH compared to PRUJ plane and forearm plane in neutral position is recalculated. Results The shape of the radial head is determined to be non-circular based on this study population (p < .001). In neutral position, the angle between the LARH and the forearm plane is 5.28° (SD: 15.09) and between the LARH and the PRUJ is 33.46° (SD: 13.91). Conclusions The position of the LARH is found to be approximately perpendicular to the forearm plane when the forearm is in neutral position and perpendicular to the PRUJ plane when the forearm is on average in 30° of pronation.

This is the first comprehensive study of the impact of biodegradation on the structure, surface potential, mechanical and piezoelectric properties of poly(3-hydroxybutyrate) (PHB) scaffolds supplemented with reduced graphene oxide (rGO) as well as cell behavior under static and dynamic mechanical conditions. There is no effect of the rGO addition up to 1.0 wt% on the rate of enzymatic biodegradation of PHB scaffolds for 30 d. The biodegradation of scaffolds leads to the depolymerization of the amorphous phase, resulting in an increase in the degree of crystallinity. Because of more regular dipole order in the crystalline phase, surface potential of all fibers increases after the biodegradation, with a maximum (361 ± 5 mV) after the addition of 1 wt% rGO into PHB as compared to pristine PHB fibers. By contrast, PHB-0.7rGO fibers manifest the strongest effective vertical (0.59 ± 0.03 pm V −1 ) and lateral (1.06 ± 0.02 pm V −1 ) piezoresponse owing to a greater presence of electroactive 𝜷-phase. In vitro assays involving primary human fibroblasts reveal equal biocompatibility and faster cell proliferation on PHB-0.7rGO scaffolds compared to pure PHB and nonpiezoelectric polycaprolactone scaffolds. Thus, the developed biodegradable PHB-rGO scaffolds with enhanced piezoresponse are promising for tissue-engineering applications.