No abstract

The deformation on the carpet texture is generally caused by foot traffic, furniture loading and soiling. The resistance of the carpet to texture distortion depends on the pile yarn characteristic and morphology. In this study, the resilience and appearance retention of carpet samples produced with drawn textured polyester pile yarns which are widely used in the carpet industry, were investigated. In this context, 6 pile yarns were produced with 3 different filament finenesses (3.13, 2.08 and 1.56 dpf) and 2 different disc types (polyurethane and ceramic). The carpet specimens were applied to compression/recovery, dynamic loading, hexapod appearance retention and soiling tests. According to the results, the carpet sample with 2.08 dpf filament fineness and produced by polyurethane disc type showed less thickness loss and better compression recovery results. Hexapod test results showed that the carpet samples with the finest filament had the lowest appearance retention levels. For soiling performance, it was observed that carpet samples with coarser filaments had slightly less staining and disc type had a no significance effect.

Uzun yıllardan bu yana günlük hayatta rahatlığı sebebiyle yaygın biçimde kullanılan bi-streç denim kıyafetler günümüzde resmi ortamlarda dahi kullanılmaya başlanmıştır. Kullanımda hareket konforu sunan bu tür ürünler için tüketici kullandığı ürünün estetik görünüm açısından da belirli bir kalite seviyesinde olmasını ister. Buruşma sonucu giysinin istenmeyen bir görüntüye sahip olması kullanıcıyı rahatsız eden bir durumdur. Bu çalışmada farklı elastan çekimi, atkı sıklığı ve doku tiplerinde üretilen bi-streç denim kumaşların buruşma özellikleri incelenmiştir. Atkı ipliği numuneleri, Ne 20/1 penye olarak, %100 pamuk hammaddesiyle ve 78 dtex doğrusal yoğunluğa sahip elastan öz ile 4 farklı elastan çekim oranında (3.07, 3.33, 3.63, 3.99) üretilmiştir. Çözgü ipliği olarak, Ne 16/1 dualcore (55 dtex PBT-44 dtex lycra ) iplik kullanılmıştır. Denim kumaş numuneleri, 3 farklı atkı sıklığında (21 tel/cm, 25 tel/cm ve 29 tel/cm), 3/1 ve 2/2 dimi desenlerinde dokunmuştur. Böylelikle 4 farklı elastan çekim oranında üretilen atkı iplikleri, 3 farklı atkı sıklığında ve 2 farklı desende, çözgü iplikleri sabit tutularak dokunmuş ve üretilen 24 adet denim kumaş numunesinin buruşma özellikleri araştırılmıştır. Çalışma sonuçlarına göre, kumaşların buruşma dayanımı özelliklerinde önemli bir farklılık görülmemiştir. Ancak, buruşma geri dönüşüm açısı test sonuçlarına uygulanan istatistiksel analiz sonucunda, atkı sıklığı ve doku tipinin buruşma geri dönüşüm açısı üzerine etkili olduğu, ancak elastan çekimindeki farklılığın etkisinin olmadığı görülmüştür. Denim clothing, which has been widely used for many years because of its comfort in daily life, has started to be used even as official wear. Consumers desire an optimum quality level regarding the aesthetic appearance from this type of high movement comfort clothing. Having wrinkles causing an undesired appearance is a disturbing situation for consumer. In this study, wrinkling properties of bi-stretch denim fabrics produced with different elastane draft, weft density and weave types were investigated. Weft yarn samples were produced from 100% cotton raw material as Ne 20/1 combed yarn with 78 dtex elastane core and with 4 different elastane draft ratios (3.07, 3.33, 3.63 and 3.99). Ne 16/1 dual-core (55 dtex PBT-44 dtex lycra ) yarn was used as warp. Denim fabric samples were produced with 3 different weft densities (21 weft/cm, 25 weft/cm and 29 weft/cm) and 2 different weave types (3/1 ve 2/2 twill weave). In doing so, wrinkling properties of the total of 24 denim fabric samples which were produced with 4 different elastane draft ratio, 3 different weft sett levels keeping the warp yarn constant and with two different pattern types were investigated. According to the results, no significant difference was seen on wrinkle recovery of the fabrics. But, as a result of the statistical analysis applied to the wrinkle recovery angle test results, it was observed that the weft density and the weave type have a statistically significant effect on the wrinkle recovery angle, whereas there ...

ÖZETGünümüzde iplik işletmeleri, iplikte oluşabilecek hataları önleme açısından önemli gelişmeler kaydetse de, kops halindeki iplikte hala önemli hatalar göze çarpmaktadır. İplik hataları, kumaş üzerinde istenmeyen görüntülere neden olduklarından, iplik bobin prosesinde etkin bir temizleme işleminden geçmeden müşteriye ulaştırılmamaktadır. Bu hataların önemli bir bölümünü kısa kalın yerler, uzun kalın yerler, ince yerler, numara varyasyonları, hatalı düğüm bölgeleri ve yabancı maddeler oluşturmaktadır. Bu çalışmada iplik yapısı, genel hata sınıflandırmaları ve iplik temizleme sistemlerinin günümüze kadar geçirmiş olduğu gelişmeler hakkında bilgi verilmiş ve dünyada en yaygın kullanılan iplik temizleme sistemleri olan Uster ve Loepfe arasında bir değerlendirme yapılmıştır. ABSTRACTToday although spinning mills have made significant improvements, there are still important yarn faults on the cops. The yarns cause many faults on the woven and knit fabrics, so that an active cleaning required for yarn cops. Short thick places, long thick places, number variations, wrong splices and foreign matters constitute the important yarn faults. Manufactured yarns should not be delivered to the customers without being cleaned effectively. In this study, information about yarn structure, general fault classifications and development of yarn cleaning systems have been informed. The most important and widely used yarn cleaning systems in the world, Uster and Loepfe are compared among themselves.