Considering that, in the context of the ecological restoration of a large number of exposed rock slopes, it is difficult for existing artificial soil to meet the requirements of mechanical properties and ecological construction at the same time, this paper investigates the stabilization benefits of polyvinyl acetate and attapulgite-treated clayey soil through a series of laboratory experiments. To study the effectiveness of polyvinyl acetate (PVA) and attapulgite as soil stabilizer, a triaxial strength test, an evaporation test and a vegetation growth test were carried out on improved soil with different amounts of PVA content (0, 1%, 2%, 3%, and 4%) and attapulgite replacement (0, 2%, 4%, 6%, and 8%). The results show that the single and composite materials of polyvinyl acetate and attapulgite can increase the peak deviator stress of the sample. The addition of polyvinyl acetate can improve the soil strength by increasing the cohesion of the sample; the addition of attapulgite improves the soil strength mainly by increasing the internal friction angle of the sample. The strength of the composite is greatly improved by increasing the cohesion and internal friction angle of the sample at the same time. The effect of adding materials increased significantly with increasing curing age. Moreover, polyvinyl acetate and attapulgite improve the soil water retention of the soil by improving the water-holding capacity, so that the soil can still ensure the good growth of vegetation under long-term drought conditions. The scanning electron microscopy (SEM) images indicated that the PVA and attapulgite of soil affect the strength characteristics of soil specimens by the reaction of PVA and water, which changes the structure of the soil and, by the interweaving of attapulgite soil particles, acts as the skeleton of the aggregate. Overall, PVA and attapulgite can effectively increase clayey soil stability by improving the cohesive force and internal friction angle of clayey soil.

Clay is one of the important base materials in slope restoration. The adhesion of clay–rock interface plays a decisive role in the repairing effect on rock slopes. Fibers and polymers are widely used as a clay improvement method in rock slope repair. In this paper, the friction effect of sisal fiber and polyvinyl acetate (PVAc)-reinforced clay was studied through the design of an indoor rock-like interface sliding model test. Using modelled test results and scanning electron microscope (SEM) images, the reinforced clay was analyzed. The test results showed that the critical sliding angle and maximum static friction force of clay decreased with the increase of moisture content. An excess of fiber content and moisture content weakens the coupling effect of fiber-anchoring clay. Fiber content of 0.8% and PVAc content of 2% had the best effect on enhancing the sliding resistance of clay and provided good adhesion for dangerous interfaces of rock slope at 35° and 45°, respectively. PVAc formed a three-dimensional networked elastic membrane structure to improve the skid resistance and dynamic friction coefficient of the clay. The results provide an effective way for soil improvement and ecological restoration.

This study investigates the potential use of polyvinyl acetate emulsion in soil strengthening with emphasis on curing condition. Molded clay specimens treated with three polymer contents of 1%, 2%, and 3% (by the weight of dry soil) are cured in dry and humid environment, respectively. Unconfined compression tests are performed on the specimens after 1, 3, and 9 days of curing, and the results are compared with that for the untreated clay specimens. This comparison shows that polyvinyl acetate polymer can enhance soil mechanical properties. It was found that the compressive strength of soil-polymer composite increases significantly with the increase of polymer content and curing time in air-drying condition, which is 24% higher than that of plain soil after 9-day curing. The role of polymer treatment is to provide soil interparticle binding, which becomes particularly important in humid environments. In curing environments of high moisture, polymer-treated soils always have greater strength, but the effectiveness of polymer treatment decreases with polymer content. The scanning electron microscopies indicate that soil structure is reinforced mostly by three-dimensional interparticle polymeric bridges. The tension in polymeric threads and textiles provides the interparticle bonding that prevents the development of cracks.