No abstract

No abstract

No abstract

A surface modification of stainless steel bearing sleeves is developed to improve the tribology characteristics at high temperature. Solid lubricant nano-and microparticles are applied for this purpose. To create the quasi-hydrodynamic lubrication regimes, the solid lubricant powder layer is made by developed pressure impregnation technique. Porous sliding bearing sleeve prototypes were made by powder metallurgy technique. The purpose of the paper is to define the friction and wear characteristics of the sleeves and to determine the influence of sealing of the sliding interface on these characteristics. It is found that application of WS 2 sold lubricant nano-and micro-particles and preservation of a particle leakage out of interface allows to achieve at the high temperature the friction coefficients comparable to those at ambient temperature.Keywords: bearing sleeves, solid lubricant, powder layer, powder metallurgy, nano-and micro-particles Opracowano modyfikację powierzchni bieżni łożysk wykonanych ze stali nierdzewnej w celu poprawy charakterystyki tribologicznej w podwyższonej temperaturze poprzez zastosowanie stałego czynnika smarnego w postaci nano-i mikro-cząstek. W celu wytworzenia warunków kwasi-hydrodynamicznego smarowania, wytworzono warstwę z proszku smarnego na drodze infiltracji ciśnieniowej. Celem pracy było wyznaczenie charakterystyki ściernej i zużyciowej bieżni oraz określenie wpływu uszczelnienia ślizgających się powierzchni na te charakterystyki. Stwierdzono, że zastosowanie WS 2 jako stałego smaru w postaci nano-i mikro-cząstek oraz zabezpieczenie wypływu z granicy fazowej pozwala uzyskać wartość współczynnika tarcia porówny-walną z otrzymywaną dla temperatury otoczenia.

In the recent years, a growth of demand for various types of self-lubricating elements of machines has been observed. A lot of parts are manufactured with the use of a powder metallurgy method. The Metal Forming Institute (INOP) in Poznan developed a modern technology, designed and made a tool for compaction of powdered parts with complex shapes and high density. The technology is being realised with a large scale equipment, which performs the forging and sizing of the sintered performs.The present work describes development of manufacturing technology and determination of mechanical and tribological properties of nanocomposites for self-lubricating bearings with a very low friction coefficient. It is envisaged to use particulate materials which consist of nano-and microparticles of solid lubricant.The study conducted aims at definition of a relationship between the microstructure and tribological properties of materials modified with solid lubricant MoS 2 nanoparticles dispersed in a technological oil. INOP's technology of nanoparticles manufacturing by RCT method (Rolling Cleavage Technology) results in that top layer of the porous bearing is modified with the nanoparticles. These layers are characterised by a low friction coefficient and considerably longer period of use. It should be noted that the stainless steel and bronze powders materials used have a good corrosion resistance. Production of the sintered bearings will disseminate the market especially in automotive and aircraft industries.Keywords: self-lubricating bearings, BROMIX, metal powders, nanoparticles, grease W ostatnich latach obserwuje się wzrost zapotrzebowania na różnego typu samosmarujące elementy maszyn. Wiele z tych detali jest wytwarzanych metodą metalurgii proszków. W INOP opracowano nowoczesną technologię i zbudowano stanowisko do kształtowania części dokładnych, o złożonych kształtach i wysokiej gęstości, z proszków metali na osnowie żelaza. Stanowisko to posiada specjalistyczną, zautomatyzowaną linię o dużej wydajności, w której realizowany jest proces dogęszczania i kalibrowania spiekanych wyprasek [1, 2].Celem prowadzonych prac naukowo -badawczych jest opracowanie technologii wytwarzania oraz określenie właściwości mechanicznych i tribologicznych nanokompozytów przeznaczonych na łożyska samosmarujące o bardzo niskim współczynniku tarcia, z wykorzystaniem materiałów zdyspergowanych w postaci nano i mikrocząstek proszków smarnych oraz proszku żelaza i brązu [1,3].Prowadzone prace miały na celu określenie właściwości mechanicznych i tribologicznych materiałów modyfikowanych nanocząstkami smarów stałych (MoS 2 ) i olejem technologicznym. Opracowana w INOP metoda wytwarzania nanocząstek metodą RCT (Rolling Cleavage Technology) prowadzi do wniosków, że zmodyfikowane tymi cząstkami warstwy wierzchnie porowatych materiałów, cechują się niskim współczynnikiem tarcia oraz znacznie dłuższym okresem ich eksploatacji. Należy zaznaczyć, że wybrane materiały na osnowy, w postaci proszków stali nierdzewnej i brązu zapewniają odporność na korozję w...