Nanoparticles of Pb1-xCdxS within the composition of 0≤x≤1 were prepared from the reaction of aqueous solution of cadmium acetate, lead acetate, thiourea, and NaOH by chemical co-precipitation. The prepared samples were characterized by UV-Vis spectroscopy(in the range 300-1100nm) to study the optical properties, AFM and SEM to check the surface morphology(Roughness average and shape) and the particle size. XRD technique was used to determine the crystalline structure, XRD technique was used to determine the purity of the phase and the crystalline structure, The crystalline size average of the nanoparticles have been found to be 20.7, 15.48, 11.9, 11.8, and 13.65 nm for PbS, Pb0.75Cd0.25S, Pb0.5Cd0.5S, Pb0.25Cd0.75S, and CdS respectively. The results indicate that crystalline structure of all prepared samples is cubic except CdS which shows hexagonal and cubic structure. The particle size was found within the range of (64.81 to 91.14) nm, with a high purity.
In this work, CdS, PbS, and Pb1-xCdxS nanoparticles with x ranged from 0.25 to 0.75 were synthesized using chemical co-precipitation mode. The pulsed laser deposition (PLD) method with laser system (Nd: YAG Laser system) was performed to make thin films of all samples which was normally performed under low gas pressure and under the following conditions; 300 mJ energy, 100 pulses, 6 Hz frequency and in the vacuum chamber on the substrates (10−2 torr). Electrical properties (D.C conductivity, Hall Effect and current-voltage measurements) of the prepared semiconductive thin films were studied using different devices. The prepared samples were characterized by UV-Vis spectroscopy (in the range 300-1100 nm) to study the optical properties, AFM and SEM to check the surface morphology (Roughness average and shape) and the particle size. XRD technique was used to determine the crystalline structure, the purity of the phase and the crystalline structure. The crystalline size averages of the nanoparticles have been found to be to 19.8, 11.0, 8.8 and 11.7 and 27.3 nm for PbS, Pb0.75Cd0.25S, Pb0.5Cd0.5S, Pb0.25Cd0.75S, and CdS respectively. The results indicate that crystalline structure of all prepared samples is cubic except CdS which shows hexagonal and cubic structure.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.