This work will show, for the first time, the effect of nicotinic acid (NA) and 2-methylnicotinic acid (MNA)on the synthesis and properties of conducting polyaniline (PANI). The work investigates the effects of sulphuric acid (H2SO4), nicotinic acid (NA), and 2-methylnicotinic acid (MNA) on the synthesis and properties of polyaniline. The results show that the preparation of polyaniline from a sulphuric acid electrolyte is faster than the preparation from nicotinic acid and 2- methylnicotinic acid electrolytes. Moreover, the electrical conductivity and thermal stability of PANI/H2SO4 were greater than PANI/NA and PANI/MNA. All the polymers prepared in this study were identified using FT-IR. Scanning electron microscopy (SEM) was used to examine the morphologies of the PANI samples, from which it was determined that PANI/H2SO4 has a fibrous and open structure with a higher porosity morphology compared to PANI/NA and PANI/MNA. The electrical conductivities of the PANI samples were measured as 1.09 S cm-1, 0.65 S cm-1 and 0.089 S cm-1 for PANI/H2SO4, PANI/NA and PANI/MNA, respectively. The thermal stability of PANI was examined using the Thermogravimetric Analysis (TGA) technique. PANI/H2SO4 was found to degrade between 450-500°C, while PANI/NA and PANI/MNA decomposed at temperatures between 300-400°C.

Physical properties of pure DESs and DESs mixed with different amounts of water were investigated by different techniques, including, rotational viscometer, Quartz Crystal Microbalance (QCM) and conductivity meter. In order to study heterogeneity of those liquids in nature. Analysis of these data showed some characteristics of heterogeneity, the extent of which depends on the number of hydrogen bond donors in the pure DES.

No abstract