Synthetic two-dimensional polymers, or bottom-up nanosheets, are ultrathin polymeric frameworks with in-plane periodicity. They can be synthesized in a direct, bottom-up fashion using atomic, ionic, or molecular components. However, few are based on carbon-carbon bond formation, which means that there is a potential new field of investigation into these fundamentally important chemical bonds. Here, we describe the bottom-up synthesis of all-carbon, π-conjugated graphdiyne nanosheets. A liquid/liquid interfacial protocol involves layering a dichloromethane solution of hexaethynylbenzene on an aqueous layer containing a copper catalyst at room temperature. A multilayer graphdiyne (thickness, 24 nm; domain size, >25 μm) emerges through a successive alkyne-alkyne homocoupling reaction at the interface. A gas/liquid interfacial synthesis is more successful. Sprinkling a very small amount of hexaethynylbenzene in a mixture of dichloromethane and toluene onto the surface of the aqueous phase at room temperature generated single-crystalline graphdiyne nanosheets, which feature regular hexagonal domains, a lower degree of oxygenation, and uniform thickness (3.0 nm) and lateral size (1.5 μm).

The nanometer-size crystallization of poly(3,4-ethylenedioxythiophene) (PEDOT) inside the hydrophobic core region of PEDOT:PSS (PSS: poly(4-styrenesulfonate)) in a solid film is found by small and wide-angle X-ray scatterings using a synchrotron radiation source. The clarified PEDOT:PSS structure indicates that a nanocrystal of PEDOT surrounded by PSS is grown in the solid film from randomly oriented PEDOT in a micelle dispersed in water during the course of film fabrication. The addition of ethylene glycol (EG) to the PEDOT:PSS water dispersion and post-treatment of the pristine film with EG both provide similar improvements in PEDOT crystallinity. The crystallite size of PEDOT increases up to a comparable size (∼4.8 nm) to the hydrophobic PEDOT core region of the micelle. The electrical conductivity of the solid film is concurrently enhanced by 2 orders of magnitude with the growing nanocrystal of PEDOT. These findings clearly demonstrate the importance of the single crystalline PEDOT assisted by EG to obtain high electrical conductivity of the PEDOT:PSS solid film.

Silk, which has excellent mechanical toughness and is lightweight, is used as a structural material in nature, for example, in silkworm cocoons and spider draglines. However, the industrial use of silk as a structural material has garnered little attention. For silk to be used as a structural material, its thermal processability and associated properties must be well understood. Although water molecules influence the glass transition of silk, the effects of water content on the other thermal properties of silks are not well understood. In this study, we prepared Bombyx mori cocoon raw fibers, degummed fibers, and films with different water contents and then investigated the effects of water content on crystallization, degradation, and water removal during thermal processing. Thermal gravimetric analyses of the silk materials showed that water content did not affect the thermal degradation temperature but did influence the water removal behavior. By increasing the water content of silk, the water molecules were removed at lower temperatures, indicating that the amount of free water in silk materials increased; additionally, the glass transition temperature decreased with increasing water plasticization. Differential scanning calorimetry and wide-angle X-ray scattering of the silk films also suggested that the water molecules in the amorphous regions of the silk films acted as a plasticizer and induced β-sheet crystallization. The plasticizing effect of water was not detected in silk fibers, owing to their lower amorphous content and mobility. The structural and mechanical characterizations of the silk films demonstrated the silk film prepared at RH 97% realized both crystallinity and ductility simultaneously. Thus, the thermal stability, mechanical, and other properties of silk materials are regulated by their water content and crystallinity.

Silk has attracted widespread attention due to its superlative material properties and promising applications. However, the determinants behind the variations in material properties among different types of silk are not well understood. We analysed the physical properties of silk samples from a variety of silkmoth cocoons, including domesticated Bombyx mori varieties and several species from Saturniidae. Tensile deformation tests, thermal analyses, and investigations on crystalline structure and orientation of the fibres were performed. The results showed that saturniid silks produce more highly-defined structural transitions compared to B. mori, as seen in the yielding and strain hardening events during tensile deformation and in the changes observed during thermal analyses. These observations were analysed in terms of the constituent fibroin sequences, which in B. mori are predicted to produce heterogeneous structures, whereas the strictly modular repeats of the saturniid sequences are hypothesized to produce structures that respond in a concerted manner. Within saturniid fibroins, thermal stability was found to correlate with the abundance of poly-alanine residues, whereas differences in fibre extensibility can be related to varying ratios of GGX motifs versus bulky hydrophobic residues in the amorphous phase.