The effect of alloy composition on the dealloying susceptibility of Ni- and Fe-based alloys is studied in near-boiling caustic solutions. A comprehensive comparison of the alloys is performed using electrochemical measurements and nanoscale characterization to evaluate dealloying behaviour. Results indicate a general increase in dealloying resistance when Ni content is increased. In alloys with similar Ni content, higher Cr content delays dealloying, while an increase in Mo content promotes dealloying. Nanoscale characterization confirms a nanoporous surface film with a core-shell ligament structure. The shell is nearly pure Ni, while ligament cores have a composition approaching that of the parent material.
Experiments have shown that the susceptibility of Ni-Cr-Fe Alloys to dealloying, and subsequently stress corrosion cracking (SCC), highly depends on alloy composition and electrochemical potential. Dealloying is defined as the selective dissolution of the more active elements in an alloy (e.g., Cr and Fe in a Ni-based alloy). A dealloying process results in a remnant nano-porous layer on the surface that could be a precursor to SCC by a mechanism known as film-induced cleavage (FIC) where cracks propagate through this layer with sufficient velocity to promote energy transmission into the underlying metal resulting in cleavage fracture. Presence of a threshold amount of a more noble element could theoretically suppress this phenomenon by surface diffusion. This was investigated further by previous researchers, and the percolation theory of materials was hypothesized that states that the more noble element in an alloy creates a percolating mass that would limit the ability to retain a connected pathway of the reactive elements from the surface given it reaches a certain threshold of the mass of the material. This percentage was estimated to be between 50-60% for most alloying systems and termed the parting limit. In this study, percolation theory and dealloying is further explored by exposing several Ni-based and Fe-based alloys with varying percentages of Ni to boiling caustic solutions (50% NaOH) and evaluating their dealloying behavior.As mentioned, dealloying highly depends on electrochemical potential and is believed to occur above a threshold potential known as the dealloying critical potential. The dealloying critical potential is defined as the condition at which a transition occurs from a “passivated” alloy surface to the sustained formation of a bi-continuous porous structure. It can be identified by running an anodic polarization scan and initially matching anodic peaks to a pH-potential diagram (Pourbaix diagram) to evaluate the potential dissolution behavior. Bench-top electrochemical measurements were conducted to find the dealloying critical potential and make a correlation between this potential and alloys’ composition. The figure attached shows the anodic polarization scan results for all alloys included in the study in 50% NaOH at 140°C. It was observed that for the samples with high Ni content (i.e., Alloy 600 and Alloy 690) there was only a single active peak, which indicates transitioning to passivation and inhibition of dealloying. All other materials were susceptible to dealloying. Electron microscopy techniques were used to analyze all the samples used in the figure after exposure to 50% NaOH at 140°C at open circuit potential (OCP) and during a potentiostatic hold at the dealloying critical potential. Scanning electron microscopy (SEM) imaging followed by energy dispersive X-ray spectroscopy (EDS) revealed varying degrees of dealloying, with low Ni-containing alloys showing greater severity.The role of dealloying as a precursor to SCC was also evaluated by utilizing U-bend samples for All...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.