The scattering spectra of single gold nanorods with aspect ratios between 2 and 4 have been examined by dark field microscopy. The results show that the longitudinal plasmon resonance (electron oscillation along the long axis of the rod) broadens as the width of the rods decreases from 14 to 8 nm. This is attributed to electron surface scattering. Analysis of the data using gamma = gamma(bulk) + Anu(F)/L(eff), where L(eff) is the effective path length of the electrons and nu(F) is the Fermi velocity, allows us to determine a value for the surface scattering parameter of A = 0.3. Larger rods with widths of 19 and 30 nm were also examined. These samples also show spectral broadening, which is attributed to radiation damping. The relative strengths of the surface scattering and radiation damping effects are in excellent agreement with recent work on spherical gold nanoparticles by Sönnichsen et al., Phys. Rev. Lett., 2002, 88, 077402; and by Berciaud et al., Nano Lett., 2005, 5, 515.
The response of gold nanorods to both thermal and ultrafast laser-induced heating has been examined. The thermal heating experiments show structural changes that occur on timescales ranging from hours to days. At the highest temperature examined (250 degrees C) the nanorods are transformed into spheres within an hour. On the other hand, no structural changes are observed in the laser-induced heating experiments up to temperatures of 700 +/- 50 degrees C. This is attributed to thermal diffusion in the laser experiments. Measurements of the period of the extensional mode of the nanorods using time-resolved spectroscopy show a significant softening at high pump laser powers. However, the decrease in the period is less than expected from bulk Young's modulus vs. temperature data.
Time-resolved spectroscopy has been used to examine the elastic properties of single crystal gold nanorods with a [100] growth direction. These rods were produce by seed-mediated growth in the presence of silver ions, using both chemical and photochemical reduction. Analysis of the experimental data yields a value of Young's modulus for the nanorods of E NR = 31 ¡ 1 GPa. This is approximately 26% smaller than the value for bulk gold of E [100] = 42 GPa. The reduction in the size of Young's modulus is consistent with our previous studies of penta-twinned, [110] growth direction nanorods, where we found E NR = 64 ¡ 2 GPa compared to E [110] = 81 GPa for bulk gold. The fact that both the single crystal and the penta-twinned nanorods show a similar reduction in E compared to the bulk values (20%-30%) shows that this effect does not arise from the presence of twin planes in the nanorods. Our data show a weak correlation between the measured values of E NR for the [100] nanorods and the surface-to-volume ratio of the rods. The larger value of Young's modulus at small size is possibly due to defect elimination. These results underscore the importance of growth direction in determining the elastic properties of nanorods and nanowires.
The response of single crystal, cubic silver particles to ultrafast laser-induced heating has been examined experimentally and theoretically. The transient absorption traces display clear modulations due to coherently excited vibrational modes. Nanocube samples with edge lengths smaller than 50 nm show a single modulation, whereas samples larger than 50 nm show two vibrational modes. The results are compared to finite element calculations, where the cubes are modeled as having cubic crystal symmetry with the principal axes parallel to the sides of the particle. The action of the laser pulse is treated in two ways, first, as creating a uniform initial strain. In this case the predominant mode excited is the breathing mode. The period of this mode is in reasonable agreement with the vibrational periods measured for the smaller cubes and with the higher frequency modulation observed for the larger cubes. A nonuniform initial strain is also considered, which could arise from nonuniform heating for particles larger than the optical skin depth of the metal. In this case the predominant mode excited is a nontotally symmetric mode. The calculated periods from this analysis are in reasonable agreement with the lower frequency modulations observed for the larger samples. The results from this study show that, to within the accuracy of these measurements, the elastic constants of cubic silver nanoparticles are the same as bulk silver.
The optical properties of two Au-Ag nanobox samples with average edge lengths of 44 and 58 nm and wall thicknesses of 6 and 8 nm, respectively, have been studied by single particle spectroscopy. The measurements gave an average line width of Gamma = 306 +/- 7 meV with a standard deviation of sigma = 30 meV for the 44-nm boxes, and Gamma = 350 +/- 9 meV with sigma = 35 meV for the 58-nm boxes. These line widths are much broader than those of gold nanorods with comparable resonance energies. The increased broadening is attributed to a combination of surface scattering of electrons, as well as increased radiation damping for the nanoboxes. Discrete dipole approximation calculations have been performed with and without surface scattering of electrons to compare with the experimental spectra. The calculations confirm that both electron-surface scattering and radiation damping are important effects in this system.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.