Pd-Cu2O core-shell nanocubes and truncated octahedra with six average sizes for each particle shape have been synthesized from 29 nm Pd nanocubes. The nanocubes have average edge lengths of 64-124 nm, while the truncated octahedra are 107-183 nm in the opposite tip distance. The core and shell composition and lattice orientation have been determined, showing the formation of single-crystalline Cu2O shells. The surface plasmon resonance (SPR) band from the Pd nanocrystal cores is barely visible. However, the Cu2O shells display facet-dependent optical properties. The Cu2O absorption band for smaller Pd-Cu2O cubes is consistently more red-shifted than somewhat larger Pd-Cu2O truncated octahedra. This work again shows that the observed facet-dependent optical phenomenon in metal-Cu2O core-shell nanocrystals is derived from the Cu2O shells. The use of 40 nm Pd cubes as cores gave uniform and size-tunable Pd-Cu2O nanocubes and truncated octahedra that display the Pd SPR band. The Pd SPR band is consistently located at 650 nm for Pd-Cu2O truncated octahedra, and 670 nm for the cubes despite large variation in the shell thickness. Both the Cu2O absorption and the Pd plasmonic band exhibit facet-dependent optical properties.
X-ray free-electron lasers provide novel opportunities to conduct single particle analysis on nanoscale particles. Coherent diffractive imaging experiments were performed at the Linac Coherent Light Source (LCLS), SLAC National Laboratory, exposing single inorganic core-shell nanoparticles to femtosecond hard-X-ray pulses. Each facetted nanoparticle consisted of a crystalline gold core and a differently shaped palladium shell. Scattered intensities were observed up to about 7 nm resolution. Analysis of the scattering patterns revealed the size distribution of the samples, which is consistent with that obtained from direct real-space imaging by electron microscopy. Scattering patterns resulting from single particles were selected and compiled into a dataset which can be valuable for algorithm developments in single particle scattering research.
The Data Descriptor incorrectly states the number of normal incidences used to generate the plot in Fig. 4b as 209. This plot was generated from 32 normal incidence cases.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.