In this study, three PCL-based polyurethane acrylates were synthesized and further formulated into twelve resins for digital light processing (DLP) 3D printing. Three PCL diols with different molecular weights were synthesized via ring-opening reaction of ε-caprolactone on diethylene glycol, with the catalyst stannous octoate. Isophorone diisocyanate (IPDI) was reacted with 2-hydroxyethyl acrylate (2-HEA) and the PCL diols form PCL-based polyurethane acrylates. Twelve resins composed of different percentages of PCL-based polyurethane acrylates, poly (ethylene glycol) diacrylate (PEGDA), propylene glycol (PPG) and photo-initiator were further printed from a DLP 3D printer. The viscosities of twelve resins decreased by 10 times and became printable after adding 30% of PEGDA. The degree of conversion for the twelve resins can reach more than 80% after the post-curing process. By changing the amount of PEGDA and PPG, the mechanical properties of the twelve resins could be adjusted. PUA530-PEG-PPG (70:30:0), PUA800-PEG-PPG (70:30:0), and PUA1000-PEG-PPG (70:30:0) were successfully printed into customized tissue scaffolds. Twelve PCL-based polyurethane photo-curable resins with tunable mechanical properties, cytotoxicity, and degradability were successfully prepared. With the DLP 3D printing technique, a complex structure could be achieved. These resins have great potential for customized tissue engineering and other biomedical application.

The aim of this research is to synthesize polycaprolactone-based polyurethanes (PCL-based PUs) that can be further used for the fabrication of guided bone regeneration (GBR) membranes with higher tensile strength and elongation at break than collagen and PTFE membranes. The PCL-based PUs were prepared by the polymerization of polycaprolactone (PCL) diol with 1,6-hexamethylene diisocyanate (HDI) at different ratios using either polyethylene glycol (PEG) or ethylenediamine (EDA) as chain extenders. The chemical, mechanical, and thermal properties of the synthesized polymers were determined using NMR, FTIR, GPC, DSC, and tensile tester. The PCL and polyurethanes were fabricated as nanofiber membranes by electrospinning, and their mechanical properties and SEM morphology were also investigated. In vitro tests, including WST-1 assay, SEM of cells, and phalloidin cytoskeleton staining, were also performed. It was shown that electrospun membranes made of PCL and PCL-HDI-PEG (2 : 3 : 1) possessed tensile strength of 19.84 MPa and 11.72 MPa and elongation at break of 627% and 362%, respectively. These numbers are equivalent or higher than most of the commercially available collagen and PTFE membrane. As a result, these membranes may have potential for future GBR applications.

In this study, five urethane acrylates (UAs), namely aliphatic urethane hexa-acrylate (87A), aromatic urethane hexa-acrylate (88A), aliphatic UA (588), aliphatic urethane triacrylate diluted in 15% HDD (594), and high-functional aliphatic UA (5812), were selected to formulate five UA-based photopolymer resins for digital light processing (DLP)-based 3D printing. Each UA (40 wt%) was added and blended homogenously with ethoxylated pentaerythritol tetraacrylate (40 wt%), isobornyl acrylate (12 wt%), diphenyl (2,4,6-trimethylbenzoyl) phosphine oxide (3 wt%), and a pink acrylic (5 wt%). Each UA-based resin specimen was designed using CAD software and fabricated using a DLP 3D printer to specific dimensions. Characteristics, mechanical properties, and cytotoxicity levels of these designed UA-based resins were investigated and compared with a commercial 3D printing denture base acrylic resin (BB base) control group at different UV exposure times. Shore hardness-measurement data and MTT assays were analyzed using a one-way analysis of variance with Bonferroni’s post hoc test, whereas viscosity, maximum strength, and modulus were analyzed using the Kruskal–Wallis test (α = 0.05). UA-based photopolymer resins with tunable mechanical properties were successfully prepared by replacing the UA materials and the UV exposure times. After 15 min of UV exposure, the 5812 and 594 groups exhibited higher viscosities, whereas the 88A and 87A groups exhibited lower viscosities compared with the BB base group. Maximum flexural strength, flexural modulus, and Shore hardness values also revealed significant differences among materials (p < 0.001). Based on MTT assay results, the UA-based photopolymer resins were nontoxic. In the present study, mechanical properties of the designed photopolymer resins could be adjusted by changing the UA or UV exposure time, suggesting that aliphatic urethane acrylate has good potential for use in the design of printable resins for DLP-type 3D printing in dental applications.

Polycaprolactone (PCL) is drawing increasing attention in the field of medical 3D printing and tissue engineering because of its biodegradability. This study developed polycaprolactone prepolymers that can be cured using visible light. Three PCL acrylates were synthesized: polycaprolactone-530 diacrylate (PCL530DA), glycerol-3 caprolactone triacrylate (Glycerol-3CL-TA), and glycerol-6 caprolactone triacrylate (Glycerol-6CL-TA). PCL530DA has two acrylates, whereas Glycerol-3CL-TA and Glycerol-6CL-TA have three acrylates. The Fourier transform infrared and nuclear magnetic resonance spectra suggested successful synthesis of all PCL acrylates. All are liquid at room temperature and can be photopolymerized into a transparent solid after exposure to 470 nm blue LED light using 1% camphorquinone as photoinitiator and 2% dimethylaminoethyl methacrylate as coinitiator. The degree of conversion for all PCL acrylates can reach more than 80% after 1 min of curing. The compressive modulus of PCL530DA, Glycerol-3CL-TA, and Glycerol-6CL-TA is 65.7 ± 12.7, 80.9 ± 6.1, and 32.1 ± 4.1 MPa, respectively, and their compressive strength is 5.3 ± 0.29, 8.3 ± 0.18, and 3.0 ± 0.53 MPa, respectively. Thus, all PCL acrylates synthesized in this study can be photopolymerized and because of their solid structure and low viscosity, they are applicable to soft tissue engineering and medical 3D printing.

Gelatin methacryloyl (GelMA) hydrogel is a photopolymerizable biomaterial widely used for three-dimensional (3D) cell culture due to its high biocompatibility. However, the drawback of GelMA hydrogel is its poor mechanical properties, which may compromise the feasibility of biofabrication techniques. In this study, a cell-laden GelMA composite hydrogel with a combination incorporating silanized hydroxyapatite (Si-HAp) and a simple and harmless visible light crosslinking system for this hydrogel were developed. The incorporation of Si-HAp into the GelMA hydrogel enhanced the mechanical properties of the composite hydrogel. Moreover, the composite hydrogel exhibited low cytotoxicity and promoted the osteogenic gene expression of embedded MG63 cells and Human bone marrow mesenchymal stem cells (hBMSCs). We also established a maskless lithographic method to fabricate a defined 3D structure under visible light by using a digital light processing projector, and the incorporation of Si-HAp increased the resolution of photolithographic hydrogels. The GelMA-Si-HAp composite hydrogel system can serve as an effective biomaterial in bone regeneration.