Abstract. Chalcopyrite copper-indium-gallium-diselenide (CIGS) nanoparticles are useful for photovoltaic applications. In this study, the synthesis of CIGS powder was examined, and the powder was successfully synthesized using a relatively simple and convenient elemental solvothermal route. From the reactions of elemental Cu, In, Se and Ga(NO3)3 powders in an autoclave with ethylenediamine as a solvent, spherical CIGS nanoparticles, with diameters ranging from 20-40 nm, were obtained using a temperature of 200°C for 36h. The structure, morphology, chemical composition and optical properties of the as-synthesized CIGS were characterized using X-ray diffraction, transmission electron microscopy, selected area electron diffraction, scanning electron microscopy, inductively coupled plasma-mass spectrometry. In this sample, the mole ratio of Cu:In:Ga:Se was equal to 0.89:0.71:0.29:2.01, and the optical band gap was found to be 1.18 eV. The solar cell obtained a power conversion efficiency of 5.62% under standard air mass 1.5 global illumination.