TIG welding enables to produce high quality weldment. However it has some problems such as shallow penetration and large distortion due to low penetration aspect ratio after welding. In order to overcome those problems, there are many ongoing studies on A-TIG welding, which use active flux. In this study, the effect of arc length and shield gas on penetration aspect ratio with melt-run welding on STS 304 6t, on which active flux was spreaded, was investigated. Arc length was changed from 1mm to 3mm, and aspect ratio became higher as arc length was decreased in this range. 100% Ar gas, Ar-H2 mixed gas, Ar-He mixed gas, and 100% He gas were used as shield gas in this study. When Ar-H 2 mixed gas, Ar-He mixed gas, and 100% He gas were applied, penetration and melting efficiency were both increased as compared with 100% Ar gas. Aspect ratio was the highest with Ar-2.5% H2 mixed gas.

Due to excellent weld quality, orbital welding with TIG is widely applied to pipe welding. But concave back bead is formed easily in overhead and inclined-up position of butt orbital welding. It is difficult to find a paper to overcome this problem. In this study, in order to make convex back bead in overhead and inclined-up position of pipe 5G welding, control method of molten pool was actively investigated. Melt run welds were conducted on thickness 4.0mm SS400 with overhead and inclined-up position and was observed the variation of bead shape after welding with the bead former developed. The height of back bead showed the trend of increase as the distance from molten pool to the bead former was decreased. Also, there is no trend in the bead width of front and back as welding position was changed or the distance from molten pool to the bead former was decreased.

Bead shape control with gas force process has been developed to overcome the concave back bead in pipe orbital welding. However, It is impossible to make a convex back bead using the existing gas nozzle, because it has high gas-consuming and low gas force. The purpose of this paper, to develop optimum shape of nozzle which to reduce the consumption of gas, maximizing the shield gas force with low cost and high productivity coincide the Green welding. In this paper venturi-type nozzle was compared with existing CP-type nozzle by TIG pulse welding in overhead position. As a result, CP-type occurs the wormholes in the overhead position, but the Venturi-type without the pore and formed a good bead appearance.

Bead shape control with gas force process has been developed to overcome the concave back bead in pipe orbital welding. However, It is impossible to make a convex back bead using the existing gas nozzle, because it has high gas-consuming and low gas force. The purpose of this paper, to develop optimum shape of nozzle which to reduce the consumption of gas, maximizing the shield gas force with low cost and high productivity coincide the Green welding. In this paper venturi-type nozzle was designed by using the Venturi meter and compared velocity, pressure, arc shape in the flat position with existing CP-nozzle. As a result, Venturi-type nozzle's maximum velocity and pressure was improved at the same flow rate. Also heat input was increased by the arc contraction in the flat position.