No abstract

No abstract

Evolution of the phase state of paramagnetic additions at various stages of synthesis and subsequent thermal treatment of glasses of the system Al 2 O 3-K 2 O-B 2 O 3 simultaneously doped with Fe 2 O 3 and MnO is studied by means of a combination of experimental techniques: Faraday rotation ͑FR͒, electron magnetic resonance ͑EMR͒, transmission electron microscopy ͑TEM͒, Mössbauer spectroscopy, and magnetic measurements. Both FR and EMR show that magnetically ordered clusters occur already at the first stage of the glass preparation. In particular, for the ratio of the Fe and Mn oxides in the charge close to 3:2, fine magnetic nanoparticles are formed with characteristics similar to those of manganese ferrite. By computer simulating the EMR spectra at variable temperatures, a superparamagnetic nature of these nanoparticles is confirmed and their mean diameter is estimated as approximately 3.2 nm. In the thermally treated glasses larger magnetic nanoparticles are formed, giving rise to FR spectra, characteristic of magnetically ordered systems, and the EMR spectra different from those in as-prepared glasses but also showing superparamagnetic narrowing. The Mössbauer spectroscopy corroborates the manganese ferrite structure of the nanoparticles and indicates their coexistence in the ferrimagnetic and superparamagnetic states. The TEM shows the presence of polydisperse nanoparticles on the background of the glass matrix, and electron diffraction of a selected region containing larger particles indicates a crystal structure close to that of MnFe 2 O 4. Energy-dispersive atomic x-ray spectra confirm that the major part of Fe and Mn introduced to the glass composition is gathered in the particles, with the concentration ratio close to 2:1, characteristic of bulk MnFe 2 O 4. Magnetic hysteresis loops of samples subjected to an additional thermal treatment demonstrate a strong increase in the coercive force, remnant magnetization, and high-field magnetic susceptibility with temperature decrease. The consistent results obtained using various techniques demonstrate that the formation of nanoparticles with characteristics close to those of MnFe 2 O 4 confers to these glasses magnetic and magneto-optical properties typical of substances possessing magnetic order.

Fe3O4@SiO2 core-shell nanoparticles (NPs) were synthesized with the co-precipitation method and functionalized with NH2 amino-groups. The nanoparticles were characterized by X-ray, FT-IR spectroscopy, transmission electron microscopy, selected area electron diffraction, and vibrating sample magnetometry. The magnetic core of all the nanoparticles was shown to be nanocrystalline with the crystal parameters corresponding only to the Fe3O4 phase covered with a homogeneous amorphous silica (SiO2) shell of about 6 nm in thickness. The FT-IR spectra confirmed the appearance of chemical bonds at amino functionalization. The magnetic measurements revealed unusually high saturation magnetization of the initial Fe3O4 nanoparticles, which was presumably associated with the deviations in the Fe ion distribution between the tetrahedral and octahedral positions in the nanocrystals as compared to the bulk stoichiometric magnetite. The fluorescent spectrum of eosin Y-doped NPs dispersed in water solution was obtained and a red shift and line broadening (in comparison with the dye molecules being free in water) were revealed and explained. Most attention was paid to the adsorption properties of the nanoparticles with respect to three dyes: methylene blue, Congo red, and eosin Y. The kinetic data showed that the adsorption processes were associated with the pseudo-second order mechanism for all three dyes. The equilibrium data were more compatible with the Langmuir isotherm and the maximum adsorption capacity was reached for Congo red.