The present paper analyzes UNS S32750 Super-Duplex Stainless Steel hot deformation behavior during processing by upsetting. The objective of this paper is to determine the optimum range of deformation temperatures, considering that both austenite and ferrite have different deformation behaviors due to their different morphology, physical, and mechanical properties. Because the capability of plastic deformation accommodation of ferrite is reduced when compared to austenite, side cracks and fissures can form during the hot deformation process. Consequently, it is important to find the optimum conditions of deformation of this type of stainless steel to establish the best processing parameters without deteriorating the material. The experimental program involved the application of hot deformation by the upsetting method on a series of samples between 1000 °C and 1275 °C, with a total degree of deformation of 30%. The resultant samples were examined by SEM-EBSD to establish and analyze the evolution of the phases present in the structure from several points of view: nature, distribution, morphology (size and shape), and their structural homogeneity. The GROD (Grain Reference Orientation Deviation) distribution map was also determined while taking into account the possible precipitation of the secondary austenite phase (γ2-phase) and the analysis of the dynamic recrystallization process according to the applied deformation temperature. The main conclusion was that UNS S32750 SDSS steel can be safely deformed by upsetting between 1050–1275 °C, with an experimented total degree of deformation of 30%.

Presently, the realization of complex, unconventional designs using efficient modalities is possible due to an increasing interest in interdisciplinary approaches: materials science, mathematics, IT, architecture, etc. Computerized techniques, among which the algorithmic/generative design is the most advanced one, that are associated with the individualized production methods are used for finding solutions for modern spatial forms with an unconventional spatial geometric shape, which are generically called “free-forms”. This work presents the design, realization and testing of a thin-walled metallic structure proposed as a light structural unit. An integrated research approach was proposed that utilized an algorithmic/digital design applied to the curved-crease-folding method with the study (at different length scales) of the metallic material behaviour after folding. An original method was proposed for the digital design and simulations. The specific mechanical behaviour of the metallic material in the elastic–plastic regime was used in this case to improve the structural performances; mechanical and structural tests were realized to analyse the behaviour of the entire structure. The results are useful for enhancing the accuracy of the digital design, the structural simulation programs and the fabrication methods.

Electrically melted and over-heated (>1500 °C) grey cast iron at less than 0.04%S, as commonly used, solidifies large amounts of carbides and/or undercooled graphite, especially in thin wall castings; this is necessary to achieve a stronger inoculation. The efficiency of Ce-bearing FeSi alloy is tested for lower ladle addition rates (0.15 and 0.25 wt.%), compared to the base and conventional inoculated iron (Ba,Ca-bearing FeSi alloy). The present work explores chill and associated structures in hypoeutectic grey iron (3.6–3.8%CE, 0.02%S, (%Mn) × (%S) = 0.013–0.016, Alres < 0.002%), in wedge castings W1, W2 and W3 (ASTM A 367, furan resin sand mould), at a lower cooling modulus (1.1–3.5 mm) that is typically used to control the quality of thin wall iron castings. Relatively clear and total chill well correlated with the standard thermal (cooling curve) analysis parameters and structural characteristics in wedge castings, at different wall thickness, displayed as the carbides/graphite ratio and presence of undercooled graphite morphologies. The difference in effects of the two inoculants addition is seen as the ability to decrease the amount of carbides and undercooled graphite, with Ce-bearing FeSi alloy outperforming the conventional inoculant, especially as the wall thickness decreased. It appears that Ce-bearing FeSi alloy could be a solution for low sulphur, electric melt, thin wall iron castings production.