This study evaluated the physical and mechanical characteristics of particleboards made of bamboo waste from the species Dendrocalamus giganteus bonded with two different types of adhesives: urea-formaldehyde (UF) and a castor oil based adhesive (M). Thus, eight types of particleboards were produced in the proportions of 6%, 8%, 10% and 12% for each adhesive. The results showed that particleboards produced with UF and M adhesives had acceptable behavior for physical tests according to the Brazilian standard NBR 14810. The results attained in mechanical tests (MOR and MOE), for all particleboards, were below the requirements for structural usage. This indicates that the residue of bamboo is a feasible raw material alternative for particleboards produced for non structural purposes, such as liners, partitions and other uses for internal seal. Regarding the adhesives, the particleboards produced with UF particleboards showed superior results for both physical and mechanical characteristics, when compared to M particleboards with the same percentage of adhesive.

The compaction rate, the relation between the density of the wood panel and the density of the wood used for producing the particles, is an indicator of the product's densification. Among the various types of wood panels, particleboards are widely employed in the lumber industry, mainly for the furniture production. This paper presents a study of the relation between the compaction rate and the properties of tensile strength perpendicular to surface, Modulus of Rupture (MOR) and Modulus of Elasticity (MOE) obtained from a static bending test, thickness swelling and water absorption (2 and 24 hours). These properties were calculated according to the Brazilian ABNT, NBR 14810 standard. Particleboards were produced using the species Pinus elliotti and adhesive ureaformaldehyde. The relation was established by a multiple linear regression, and the most appropriate statistical models were determined. The estimated models indicate statistically significant effects of water absorption in 2 hours and MOR in the particleboards' compaction rate

In the worldwide market of particleboard production, the use of alternative raw materials is increasing, due to high demand and lack of traditional raw material, despite efforts of reforestation. In Brazil, the main agricultural commodity is sugarcane due to the copious production of sugar and ethanol. In the state of São Paulo alone approximately 140 million tons of sugarcane bagasse are produced every year, from which around 70% is burned for energy production, not adding value to the residue and generating pollution to the environment; and the other 30% is sold for composting. The objective of this work is to add value to the sugarcane bagasse by using it as a raw material for particleboard production to be employed as flooring in the area of civil construction. To achieve this, the present research characterized the physical and mechanical characteristics of the particleboards with the following alternative raw materials: sugarcane bagasse and leaves of bamboo. Particleboards were produced to reach high density (0.8 g/cm 3 ) using the resin (bi-component) polyurethane castor oil. Tests for abrasion, roughness and resistance to denting and wear (Janka hardness) verified that the addition of leaves of bamboo in the mixtures, contrary to what was expected, did not confer a greater degree of resistance to the particleboards. Lastly, the results showed that sugarcane bagasse is a viable raw material alternative for the production of particleboards, intended to be used as products and flooring.

The objective of this study was to evaluate the density, density profile, water swelling and absorption, modulus of elasticity and rupture from static bending, and tensile strength of experimental medium-density fiberboards manufactured using Dendrocalamus giganteus (Munro bamboo). The fiber production was carried out through the chemo-thermo-mechanical pulping process with four different conditions. The panels were made with 10% urea formaldehyde resin based on dry weight of the fibers, 2.5% of a catalyzer (ammonium sulfate) and 2% paraffin. The results indicate that treatments with the highest alkali (NaOH) percentage, time and splinter heating temperature improved the physical properties of the panels. The root-fiber interface was evaluated through scanning electron microscopy in fracture zones, which revealed fibers with thick, inflexible walls. The panels' mechanical properties were affected due to the fiber wall characteristics and interaction with resin. Giant bamboo fiber has potential for MDF production, but other studies should be carried out.

The purpose of this study was to evaluate the physical and mechanical properties of particleboard made with pruning wastes from Ipê (Tabebuia serratifolia) and Chapéu-de-Sol (Terminalia catappa) trees. Particleboards were prepared with both wood species, using all the material produced by grinding the pruning wastes. The particleboards had dimensions of 45 × 45 cm, a thickness of approximately 11.5 mm and an average density of 664 kg/m3. A urea-formaldehyde adhesive was used in the proportion of 12% of the dry particle mass. The particleboards were pressed at a temperature of 130°C for 10 mins. The physical and mechanical properties analyzed were density, moisture content, thickness swelling, percentage of lignin and cellulose, modulus of resilience, modulus of elasticity and tensile strength parallel to the grain, accordingly to the standards NBR 14810 and CS 236-66 (1968). The particleboards were considered to be of medium density. The particle size significantly affected the static bending strength and tensile strength parallel to the grain. Ipê presented better results, demonstrating a potential for the production and use of particleboard made from this species.