This paper presents the research results of the copolymer structure and properties of 2-hydroxyethylmethacrylate (HEMA) with polyvinylpyrrolidone (PVP) and their hydrogels, obtained by block polymerization in the presence of iron sulfate (II). By the methods of chemical analysis, IR spectroscopy, Thermogravimetric (TG) and Differential Thermal Analysis (DTA), the course of grafted copolymerization of HEMA on PVP with the formation of a cross-linked copolymer was confirmed. The results received by scanning electron microscopy showed that due to the copolymerization of HEMA with PVP, macroporous hydrogels with a pore size of 10–30 μm were obtained. The peculiarities of the structure formation of the obtained copolymers depending on the initial composition formulation were established and their structural parameters were investigated: PVP grafting efficiency, PVP content in copolymer, molecular weight of internodal fragment of polymer network, crosslinking degree, and crosslinking density. The interrelation of sorption–diffusion, physical–mechanical and thermophysical properties along with the structure of the obtained materials was proved. It was shown that with the increasing PVP content in the original composition, the efficiency of its grafting and crosslinking density of the polymer network decreased, but the surface hardness, heat resistance, sorption capacity of copolymers in the dry state, as well as ion permeability and elasticity in the swollen state increased, while their tensile strength deteriorated. It is proved that by changing the original composition formulation it is possible to change the structure and hence the properties of the copolymers in the desired direction.

This paper presents the result of a study evaluating the influence of alternative path generation strategy on structure and some mechanical properties of parts produced by Fused Deposition Modeling (FDM) technology. Several scientific investigations focused on resolving issues in FDM parts by modifying a path generation strategy to optimize its mechanical properties. In this study, an alternative strategy was proposed with the intention of minimizing internal voids and, thus, to improve mechanical properties. Polycarbonate samples made by this alternative path generation strategy were subjected to tensile strength test and metro-tomography structure evaluation. The results reveal that the structure observed on build models differs from a structure expected from path generation predicted by software Insight 9.1. This difference affected the tensile strength of samples.

The aim of the present work is to investigate the effect of halloysite nanotubes (HNT) on the mechanical properties of low-density polyethylene composites modified by maleic anhydride-grafted PE (PE-graft-MA). Polyethylene nanocomposites were prepared using an injection molding machine, Arburg Allrounder 320 C 500–170; the HNT content was varied at 0 wt %, 2 wt %, 4 wt % and 6 wt %, and the PE-graft-MA content was varied at 5 wt %. The composites were examined for their ultimate tensile stress, strain at ultimate stress, hardness, impact strength, melt flow rate, heat deflection temperature, Vicat softening temperature, crystallinity degree and phase transition temperature. It was found that the addition of halloysite nanotubes to low-density polyethylene (LDPE) led to an increased heat deflection temperature (HDT, up to 47 °C) and ultimate tensile strength (up to 16.00 MPa) while the Vicat softening temperature, strain at ultimate stress, impact strength and hardness of examined specimens slightly decreased. Processing properties of the materials specified by the melt flow rate (MFR) deteriorated almost twice. The results have demonstrated that the nanoparticles can reinforce enhance LDPE at low filler content without any considerable loss of its ductility, but only when halloysite nanotubes are superbly distributed in the polyethylene matrix.

The synthesis and study of metal-containing hydrogels, particularly those filled with nickel nanoparticles, is currently of interest to many researchers. This paper presents the results of an investigation of the structure and properties of Ni(0)-filled composites on the basis of 2-hydroxyethylmethacrylate copolymers (HEMA) with polyvinylpyrrolidone (PVP) and their hydrogels. The authors of the article are the first who propose the method to produce these materials by combining the processes of polymer matrix synthesis and a reduction of Ni2+ ions. Synthesis is carried out in one stage without complicated equipment and is technologically simple. It is determined by thermometric research that the temperature conditions required for the chemical reduction of Ni2+ are achieved due to the heat released during the exothermic reaction of HEMA polymerization in the presence of PVP. With the help of Fourier transform infrared analysis, and thermogravimetric and differential-thermal analysis, the formation of a crosslinked graft copolymer based on HEMA and PVP was confirmed, and its structural parameters, including the efficiency of PVP grafting, PVP content in the copolymer, and the molecular weight of the interstitial fragment of the polymer network, were investigated. The results obtained with scanning electron microscopy revealed that the size of the Ni(0) particles is about 500 nm. X-ray structural analysis of the composites obtained confirmed the existence of metal nickel particles. The strength, elastic, sorption, electrical, and magnetic properties of the obtained composites in the solid (dry) and elastic (swollen) physical states, depending on the composition of the copolymer and the content of the metal filler, have been investigated.

No abstract