This paper is focused on the preparation of novel hybrid polymer composite materials for 3D filaments. As the reinforcing filler, expanded graphite, carbon fibers, and combinations thereof were used in various ratios up to 10%. The mechanical and thermal properties of virgin and recycled polyethylene phthalate glycol-modified (PETG) composite materials were determined. Almost all prepared composite materials were suitable for 3D printing and they have enhanced mechanical properties compared to the neat PETG matrices. Addition of the fillers to both polymer matrices has an only slight effect on the thermal stability, but the addition of carbon fibers significantly reduced the thermal expansion coefficient. The composites from cheaper recycled PETG have comparable properties to virgin PETG composites, which is of economic and ecological importance. New and cheaper materials can help expand 3D printing to manufacturing plants and the use of 3D printers for special applications.

No abstract

In this work, the high temperature oxidation behavior of Al71Co29 and Al76Co24 alloys (concentration in at.%) is presented. The alloys were prepared by controlled arc-melting of Co and Al granules in high purity argon. The as-solidified alloys were found to consist of several different phases, including structurally complex m-Al13Co4 and Z-Al3Co phases. The high temperature oxidation behavior of the alloys was studied by simultaneous thermal analysis in flowing synthetic air at 773–1173 K. A protective Al2O3 scale was formed on the sample surface. A parabolic rate law was observed. The rate constants of the alloys have been found between 1.63 × 10−14 and 8.83 × 10−12 g cm−4 s−1. The experimental activation energies of oxidation are 90 and 123 kJ mol−1 for the Al71Co29 and Al76Co24 alloys, respectively. The oxidation mechanism of the Al-Co alloys is discussed and implications towards practical applications of these alloys at high temperatures are provided.

No abstract

No abstract